Análise da pulsação térmica do processo TIG na soldagem da liga AA6063T6

• Ano de defesa: 2014
• Autor(a) principal: Macedo Filho, Vanderlei Guilherme de [UNESP]
• Tipo de documento: Dissertação
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: Universidade Estadual Paulista (Unesp)
• Palavras-chave em Português: Soldagem; Aluminio; Ligas de aluminio; Welding
• Link de acesso: http://hdl.handle.net/11449/123836; http://www.athena.biblioteca.unesp.br/exlibris/bd/cathedra/28-05-2015/000823683.pdf

For some aluminum alloys, especially 6xxx (Al-Mg-Si) series, the able to develop solidification cracking in AC-GTAW welding is a constant preoccupation. In operation scope the minimal incident of this, or even its elimination, has been done by methods that are able to modify the microestrural in melted pool zone and thermic affected zone by agitation of the melted pool. IN AC-GTAW welding process, recourses applied for agitation of the melted pool, and following microestrutural depuration, are the electro polarity inversion frequency and thermic pulse cycle frequency. Be sure that this knowledge and its correct application for decrease solidification cracking is important to the process engineering and it constitutes an important technical information for available. On this work, the AC-GTAW thermic pulse welding on plate was used on AA6063T6 aluminium alloy analysis results for 50,100 and 200Hz electro polority inversion frequency, in agreement with 0,5;1,0;1,7 and 5,0Hz thermic pulse cycle frequency. The Houldcroft weldability test was enlargement used how important tool for this analysis, in agreement with macro and microestrutural analysis of melted pool zone and thermic affected zone. Althogh the solidification cracking formation has not been eliminated, it was possible to verify their decreasing due by increase of the electro polarity inversion frequency and increase thermic pulse cycle frequency, followed by grain depuration in melted pool zone and thermic affected zone