Influência do tempo de endurecimento no comportamento físico e biológico de sete cimentos endodônticos

• Ano de defesa: 2014
• Autor(a) principal: França, Monique Costa Moreira [UNESP]
• Tipo de documento: Dissertação
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: Universidade Estadual Paulista (Unesp)
• Palavras-chave em Português: Citotoxicidade; Adesão; Cimentos dentarios; Dental cements
• Link de acesso: http://hdl.handle.net/11449/127668; http://www.athena.biblioteca.unesp.br/exlibris/bd/cathedra/01-09-2015/000843350.pdf

Objective: The aim of this study was to evaluate the influence of curing time on physical (push-out test) and biological properties (XTT, MNT) of seven sealers: Apexit Plus, Royal Seal, Endo Rez, Roeko Seal, AH Plus, Endomethasone, and bioceramic cement iRoot SP. Material and Methods: To the citotoxity analysis (XTT), fibroblasts of the human periodontal ligament were used (PDLF). To the number of micronuclei (MNT), this study evaluated cell cultures exposed to dilutions of the tested sealers, among them from causing excessive cytotoxic effects on V79 cells. To push-out test was used one hundred and forty single-rooted teeth which had the crowns removed. The root canals were prepared biomechanically with the rotary system Mtwo (VDW GmbH, München, Alemanha) until to series number 702 to file 25 mm (25-40). Throughout the biomechanical preparation, the canals were irrigated with 2 ml of sodium hypochlorite. The specimens were sectioned in slices of 2 mm in cervical, middle and apical. The push-out test was performed at speed of 1 mm/min and 50 kgf load cell. The tests were evaluated after 24 h, 72 h, 1 week, 1 month, 3 months, 6 months and one year after manipulation. Data were analyzed by Kruskal-Wallis and Dunn test (p = 0.05). Results: IRooot SP, Roeko Seal, Apexit Plus, AH plus and Real Seal showed no cytotoxicity in PDLF cells. AH plus, Real Seal, IRooot SP and Endomethasone N showed no genotoxicity. Roeko Seal and Apexit Plus have shown to be genotoxic and EndoRez showed high genotoxicity. Roeko Seal, IRooot SP and EndoRez had lower bond strength in the apical, middle and cervical thirds in both the 15-day and 1 year analysis. Apexit Plus, Endomethasone N, Real Seal and AH plus had a satisfactory bond strength after 1 year in all thirds. Conclusion: It is conclude that AH plus and Real Seal were the sealer with lower cytotoxicity and genotoxicity, with good values of bond strength in all third, keeping as the material of choice for....