Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere

Detalhes bibliográficos
Autor(a) principal: Murthy,Yogesh Iyer
Data de Publicação: 2020
Outros Autores: Gandhi,Sumit, Kumar,Abhishek
Tipo de documento: Artigo
Idioma: eng
Título da fonte: Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
Texto Completo: http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042020000400004
Resumo: A comparative study of the corrosion behavior of pure magnesium and AZ91D anodes in reinforced cement concrete was undertaken in the present work. The steel reinforcements were electrochemically kept in contact with these anodes in a chloride atmosphere, and the half-cell potential drop was observed. Bare steel reinforcements were tied to the anodes and were also kept in a high chloride atmosphere to test the mechanical properties. The yield stress and ultimate tensile stress were found to decrease by approximately 50 MPa, while the reduction in percentage elongation was approximately 25% for reinforcements tied to AZ91D and pure Mg, at the end of 80 days, compared to the fresh steel reinforcement. The rate of corrosion of pure Mg was reportedly slightly higher compared to AZ91D, due to the presence of inter-metallics, as inferred through micro-graphs.
id RCAP_df85c07d21b166bddea39ad5fb0aee96
oai_identifier_str oai:scielo:S0872-19042020000400004
network_acronym_str RCAP
network_name_str Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
repository_id_str https://opendoar.ac.uk/repository/7160
spelling Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmospherecathodic protectionAZ91Dmechanical propertieshalf-cell potentialmicro-characterizationinter-metallicsA comparative study of the corrosion behavior of pure magnesium and AZ91D anodes in reinforced cement concrete was undertaken in the present work. The steel reinforcements were electrochemically kept in contact with these anodes in a chloride atmosphere, and the half-cell potential drop was observed. Bare steel reinforcements were tied to the anodes and were also kept in a high chloride atmosphere to test the mechanical properties. The yield stress and ultimate tensile stress were found to decrease by approximately 50 MPa, while the reduction in percentage elongation was approximately 25% for reinforcements tied to AZ91D and pure Mg, at the end of 80 days, compared to the fresh steel reinforcement. The rate of corrosion of pure Mg was reportedly slightly higher compared to AZ91D, due to the presence of inter-metallics, as inferred through micro-graphs.Sociedade Portuguesa de Electroquímica2020-06-01info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/articletext/htmlhttp://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042020000400004Portugaliae Electrochimica Acta v.38 n.4 2020reponame:Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)instname:FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologiainstacron:RCAAPenghttp://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042020000400004Murthy,Yogesh IyerGandhi,SumitKumar,Abhishekinfo:eu-repo/semantics/openAccess2024-02-06T17:07:32Zoai:scielo:S0872-19042020000400004Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireinfo@rcaap.ptopendoar:https://opendoar.ac.uk/repository/71602025-05-28T12:56:43.812826Repositórios Científicos de Acesso Aberto de Portugal (RCAAP) - FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologiafalse
dc.title.none.fl_str_mv Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere
title Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere
spellingShingle Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere
Murthy,Yogesh Iyer
cathodic protection
AZ91D
mechanical properties
half-cell potential
micro-characterization
inter-metallics
title_short Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere
title_full Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere
title_fullStr Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere
title_full_unstemmed Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere
title_sort Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere
author Murthy,Yogesh Iyer
author_facet Murthy,Yogesh Iyer
Gandhi,Sumit
Kumar,Abhishek
author_role author
author2 Gandhi,Sumit
Kumar,Abhishek
author2_role author
author
dc.contributor.author.fl_str_mv Murthy,Yogesh Iyer
Gandhi,Sumit
Kumar,Abhishek
dc.subject.por.fl_str_mv cathodic protection
AZ91D
mechanical properties
half-cell potential
micro-characterization
inter-metallics
topic cathodic protection
AZ91D
mechanical properties
half-cell potential
micro-characterization
inter-metallics
description A comparative study of the corrosion behavior of pure magnesium and AZ91D anodes in reinforced cement concrete was undertaken in the present work. The steel reinforcements were electrochemically kept in contact with these anodes in a chloride atmosphere, and the half-cell potential drop was observed. Bare steel reinforcements were tied to the anodes and were also kept in a high chloride atmosphere to test the mechanical properties. The yield stress and ultimate tensile stress were found to decrease by approximately 50 MPa, while the reduction in percentage elongation was approximately 25% for reinforcements tied to AZ91D and pure Mg, at the end of 80 days, compared to the fresh steel reinforcement. The rate of corrosion of pure Mg was reportedly slightly higher compared to AZ91D, due to the presence of inter-metallics, as inferred through micro-graphs.
publishDate 2020
dc.date.none.fl_str_mv 2020-06-01
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/article
format article
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042020000400004
url http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042020000400004
dc.language.iso.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042020000400004
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv text/html
dc.publisher.none.fl_str_mv Sociedade Portuguesa de Electroquímica
publisher.none.fl_str_mv Sociedade Portuguesa de Electroquímica
dc.source.none.fl_str_mv Portugaliae Electrochimica Acta v.38 n.4 2020
reponame:Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
instname:FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologia
instacron:RCAAP
instname_str FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologia
instacron_str RCAAP
institution RCAAP
reponame_str Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
collection Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
repository.name.fl_str_mv Repositórios Científicos de Acesso Aberto de Portugal (RCAAP) - FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologia
repository.mail.fl_str_mv info@rcaap.pt
_version_ 1833593274548355072

Registros relacionados