Efeito de ambientes hostis na resistência ao impacto de aço ao carbono produzido por Wire-Arc Additive Manufacturing (WAAM)

Bibliographic Details
Main Author: Mendes, Rodrigo Bernardo de Lopes
Publication Date: 2022
Format: Master thesis
Language: por
Source: Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
Download full: https://hdl.handle.net/10316/102943
Summary: Dissertação de Licenciatura em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
id RCAP_c54c88d2b6ca039a2b0508a4d1c74343
oai_identifier_str oai:estudogeral.uc.pt:10316/102943
network_acronym_str RCAP
network_name_str Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
repository_id_str https://opendoar.ac.uk/repository/7160
spelling Efeito de ambientes hostis na resistência ao impacto de aço ao carbono produzido por Wire-Arc Additive Manufacturing (WAAM)Effect of hostile environments on the impact strength of carbon steel produced by Wire-Arc Additive Manufacturing (WAAM)Wire-Arc Additive ManufacturingCondições de DegradaçãoEnsaio CharpyImpactoAço Carbono.Wire-Arc Additive ManufacturingDegradation ConditionsCharpy TestImpactCarbon SteelDissertação de Licenciatura em Engenharia Mecânica apresentada à Faculdade de Ciências e TecnologiaA presente Dissertação de Mestrado tem como principal propósito analisar a influência de ambientes hostis na resistência ao impacto de aço carbono fabricado por Wire-Arc Additive Manufacturing (WAAM). Este estudo tem como base a bibliografia já existente na temática da degradação e do WAAM, destacando-se da mesma, na medida em que são analisadas novas condições de degradação do material cujos efeitos no comportamento mecânico, até aqui, não são, ainda, bem conhecidos.Desta forma, estudou-se o efeito de ambientes hostis na resistência ao impacto, segundo a influência da solução de degradação (NaCl e HCl), do tempo de imersão (0 dias, 15 dias e 30 dias), da aplicação ou não de tensão elétrica nas mesmas, das condições de deposição das placas (diferença de espessura) e da orientação do seccionamento dos provetes(vertical e horizontal). O parâmetro da energia absorvida, que se traduz na resistência ao impacto, foi medido através da fratura total dos provetes por intermédio de Ensaio Charpy, sendo que, posteriormente, foi analisada a superfície de fratura, por microscopia eletrónica de varrimento, de forma a avaliar a influência das condições descritas nos mecanismos de rotura dos provetes. Após os resultados foi possível concluir que o aumento do tempo de degradação tem uma influência acentuada na resistência ao impacto, uma vez que, analisando a mesma condição de degradação, foi possível visualizar um dano mais elevado nas amostras que foram degradadas durante mais tempo. No que diz respeito à aplicação de tensão elétrica, também foi possível concluir que provoca um dano mais acentuado nos provetes a ela sujeitos. Em termos da solução de degradação utilizada, verificou-se que o HCl ataca o provete de uma forma mais efetiva que o NaCl, provocando, inclusive, com maior facilidade a formação de óxidos. Por fim e em relação, às condições de fabrico e à orientação do seccionamento, não foi possível tirar uma conclusão objetiva devido à existência provável de variabilidades inerentes ao procedimento experimental. No caso da orientação do seccionamento pensa-se que a dificuldade da obtenção de conclusões gerais, se deve ao facto da porosidade do material não estar distribuída de forma homogénea.The main purpose of this Master's Dissertation is to analyze the influence of hostile environments on impact resistance of carbon steel manufactured by Wire-Arc Additive Manufacturing (WAAM). This study is based on the existing bibliography on the subject of degradation and WAAM, standing out from the same, insofar as new solutions and degradation conditions are used in a material that, until now, the behavior, when subjectedto these environments, was not known.In this way, the effect of hostile environments on impact resistance was studied, according to the influence of the degradation solution (NaCl and HCl), the immersion time (0 days, 15 days, and 30 days), the application or not of an electrical voltage in the solutions, the manufacturing conditions of the plates (difference thickness) and the orientation of the sectioning of the specimens (vertical and horizontal). The parameter of absorbed energy, which translates into impact resistance, was measured through the fracture of the specimens through the Charpy Test, and, later, the fracture surface was analyzed by scanning electron microscopy, in order to evaluate the influence of the described conditions, in the failure mechanisms of the specimens.As a result, it was possible to conclude that the increase in the degradation time has a strong influence on the impact resistance, since, analyzing the same degradation condition, it was possible to visualize a higher damage in the samples that were degraded for a longer time. Regarding to the application of an electrical voltage, it was also possible to conclude that it causes more damage to the specimens subjected to it. In terms of the used degradation solution, it was concluded that HCl attacks the specimens in a more effective way than NaCl,causing more easily the formation of oxides. Finally, regarding the manufacturing conditions and the orientation of the sectioning, a general objective conclusion was not taken due to the existence of variability inherent to the experimental procedure. In the case of the orientation of the sectioning, it is believed that the difficulty in obtaining general conclusions is due to the fact that the porosity of the material was not homogeneously distributed.2022-09-26info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttps://hdl.handle.net/10316/102943https://hdl.handle.net/10316/102943TID:203079124porMendes, Rodrigo Bernardo de Lopesinfo:eu-repo/semantics/openAccessreponame:Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)instname:FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologiainstacron:RCAAP2022-10-19T20:31:45Zoai:estudogeral.uc.pt:10316/102943Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireinfo@rcaap.ptopendoar:https://opendoar.ac.uk/repository/71602025-05-29T05:52:31.808759Repositórios Científicos de Acesso Aberto de Portugal (RCAAP) - FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologiafalse
dc.title.none.fl_str_mv Efeito de ambientes hostis na resistência ao impacto de aço ao carbono produzido por Wire-Arc Additive Manufacturing (WAAM)
Effect of hostile environments on the impact strength of carbon steel produced by Wire-Arc Additive Manufacturing (WAAM)
title Efeito de ambientes hostis na resistência ao impacto de aço ao carbono produzido por Wire-Arc Additive Manufacturing (WAAM)
spellingShingle Efeito de ambientes hostis na resistência ao impacto de aço ao carbono produzido por Wire-Arc Additive Manufacturing (WAAM)
Mendes, Rodrigo Bernardo de Lopes
Wire-Arc Additive Manufacturing
Condições de Degradação
Ensaio Charpy
Impacto
Aço Carbono.
Wire-Arc Additive Manufacturing
Degradation Conditions
Charpy Test
Impact
Carbon Steel
title_short Efeito de ambientes hostis na resistência ao impacto de aço ao carbono produzido por Wire-Arc Additive Manufacturing (WAAM)
title_full Efeito de ambientes hostis na resistência ao impacto de aço ao carbono produzido por Wire-Arc Additive Manufacturing (WAAM)
title_fullStr Efeito de ambientes hostis na resistência ao impacto de aço ao carbono produzido por Wire-Arc Additive Manufacturing (WAAM)
title_full_unstemmed Efeito de ambientes hostis na resistência ao impacto de aço ao carbono produzido por Wire-Arc Additive Manufacturing (WAAM)
title_sort Efeito de ambientes hostis na resistência ao impacto de aço ao carbono produzido por Wire-Arc Additive Manufacturing (WAAM)
author Mendes, Rodrigo Bernardo de Lopes
author_facet Mendes, Rodrigo Bernardo de Lopes
author_role author
dc.contributor.author.fl_str_mv Mendes, Rodrigo Bernardo de Lopes
dc.subject.por.fl_str_mv Wire-Arc Additive Manufacturing
Condições de Degradação
Ensaio Charpy
Impacto
Aço Carbono.
Wire-Arc Additive Manufacturing
Degradation Conditions
Charpy Test
Impact
Carbon Steel
topic Wire-Arc Additive Manufacturing
Condições de Degradação
Ensaio Charpy
Impacto
Aço Carbono.
Wire-Arc Additive Manufacturing
Degradation Conditions
Charpy Test
Impact
Carbon Steel
description Dissertação de Licenciatura em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
publishDate 2022
dc.date.none.fl_str_mv 2022-09-26
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/10316/102943
https://hdl.handle.net/10316/102943
TID:203079124
url https://hdl.handle.net/10316/102943
identifier_str_mv TID:203079124
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.source.none.fl_str_mv reponame:Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
instname:FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologia
instacron:RCAAP
instname_str FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologia
instacron_str RCAAP
institution RCAAP
reponame_str Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
collection Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
repository.name.fl_str_mv Repositórios Científicos de Acesso Aberto de Portugal (RCAAP) - FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologia
repository.mail.fl_str_mv info@rcaap.pt
_version_ 1833602503466287104

Similar Items