Effect of Gadolinium Content on the Corrosion Behavior of Magnesium Alloys in 1 wt.% NaCl Solution

• Autor(a) principal: Zidane,N.
• Data de Publicação: 2015
• Outros Autores: Ait Albrimi,Y., Ait Addi,A., Ait Akbour,R., Douch,J., Nahle,A., Hamdani,M.
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
• Texto Completo: http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042015000500004
• topic: magnesium alloys; biomaterials; corrosion resistance; gadolinium alloying

The aim of this work was to study the effect of gadolinium content on the corrosion behavior of magnesium alloys in 1 wt.% NaCl solution at 21.5 (±0.5) °C. Four Mg-Gd alloys, namely Mg-2 wt.% Gd, Mg-5 wt.% Gd, Mg-10 wt.% Gd, and Mg-15 wt.% Gd, were studied. Weight loss measurements, potentiodynamic tests, electrochemical impedance spectroscopy, XR diffraction, and scanning electron microscopy combined with energy-dispersive X-ray spectroscopy (SEM-EDS) were performed on the four Mg-Gd samples. The results showed the influence of the Gd content on the corrosion behavior of these alloys in 1wt.% NaCl solution. The corrosion resistance of the Mg-Gd alloys was improved with the introduction of 10 wt.% Gd in Mg matrix. Thus, weight loss and electrochemical measurements revealed the better corrosion resistance for Mg10 wt.% Gd alloy. Further addition of Gd exceeding 10 wt.% in a magnesium matrix reduces the corrosion resistance of Mg-alloy and induces an incremental increase in the corrosion rate.