Mechanical properties and corrosion behaviours of the as-cast ZK40 alloys modified with individual additions of CaO, Gd, Nd and Y

Detalhes bibliográficos
Ano de defesa: 2016
Autor(a) principal: Buzolin, Ricardo Henrique
Orientador(a): Não Informado pela instituição
Banca de defesa: Não Informado pela instituição
Tipo de documento: Dissertação
Tipo de acesso: Acesso aberto
Idioma: eng
Instituição de defesa: Biblioteca Digitais de Teses e Dissertações da USP
Programa de Pós-Graduação: Não Informado pela instituição
Departamento: Não Informado pela instituição
País: Não Informado pela instituição
Palavras-chave em Português:
CaO
Gd
Nd
Y
Link de acesso: http://www.teses.usp.br/teses/disponiveis/18/18158/tde-13012017-093623/
Resumo: The effect of individual additions of calcium oxide (CaO), Gd, Nd and Y was investigated on the microstructure, mechanical properties and corrosion resistance of the as-cast ZK40 alloy. The microstructural features were analised using optical, scanning and transmission electron microscopy, X-ray diffraction and Scanning Kelvin Atomic Probe Force Microscopy. The compressive and tensile behaviours of the as-cast alloys at room temperature were investigated. Electrochemical Impedance Spectroscopy, hydrogen evolution and weight loss under immersion in 0.5 wt.% NaCl solution were used to evaluate the corrosion behaviour. The results of the mechanical and corrosion tests were correlated with the microstructures. The 2 wt.% Gd addition enhanced the ductility, while the Nd addition resulted in deterioration in mechanical properties. The addition of 2 wt.% Gd and 1 wt.% Y resulted in the improvement of the ductility. The addition of CaO did not affect the mechanical properties while the 2 wt.% Nd deteriorate it. The 1 wt.% Y addition enhanced the ductility. The CaO addition did not caused enhancement in mechanical properties. The corrosion behaviour was enhanced with the addition of CaO and Gd. The modification of ZK40 with Gd opens up new perspectives in the development of Mg-Zn based alloys.