Análise estrutural e bioquímica da hidroxiapatita submetida ao tratamento com fluoreto e polifosfatos

• Ano de defesa: 2014
• Autor(a) principal: Amaral, Jackeline Gallo do [UNESP]
• Tipo de documento: Tese
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: Universidade Estadual Paulista (Unesp)
• Palavras-chave em Português: Polifosfatos; Fluoretos; Saliva; Durapatita; Polyphosphates
• Link de acesso: http://hdl.handle.net/11449/123775; http://www.athena.biblioteca.unesp.br/exlibris/bd/cathedra/20-05-2015/000828991.pdf

This study evaluated the effect of sodium trimetaphosphate (TMP) and sodium hexametaphosphate (HMP) associated or no with fluoride (F) on the structure and dissolution of hydroxyapatite (HA). For this purpose, the study was divided into three subprojects. In Subprojects 1 and 2, synthetic HA powder (n=6) was treated with solutions containing TMP varying at 0-10% associated with 0, 100, 250, 500 (Subproject 1) and 0, 1100, 4500 and 9000 ppm F (Subproject 2) and submitted to a pH cycle. Afterwards, alkali- and acid soluble F, Ca and P were determined in/on HA, and P and F in the supernatants. Samples were analyzed by infrared spectroscopy (FTIR), X-ray diffraction (XDR) and energy-dispersive X-ray spectroscopy (EDX). In Subproject 3, HA discs were used to assess the dissolution rate of HA using a pHstat system. HA discs were treated with 1100 ppm F, 1% and 8% of HMP or TMP and 1100 ppm F associated with 1% and 8% of HMP or TMP, totaling 9 groups (n=8). The influence of a salivary pellicle on HA dissolution was also assessed. HA discs were kept in pooled human saliva before treatment with deionised water and 1100 ppm F associated with 1% and 8% of HMP or TMP, totaling 5 groups (n=8). The post-treatment dissolution rate was determined from three consecutive 30-min assays. Data were submitted to ANOVA, Student-Newman-Keuls' test and Pearson's correlation coefficient (Subprojects 1 and 2), and to ANOVA and Fisher and Holm- Sidak methods (Subproject 3) (α=0.05). Ca/P ratios values were higher for the fluoride solutions when compared with the no F and TMP groups and dependent of the F:TMP ratio used (p<0.05). The overall trend was that alkali-soluble F deposition was directly related to TMP concentrations in the treatment solutions, while acidsoluble incorporation was inversely related to TMP...