Efeito do laser ER:YAG e ponta diamantada na morfologia da camada híbrida obtida com um adesivo autocondicionante: resistência de união ao microcisalhamento análise por MEV e MLCF

Detalhes bibliográficos
Ano de defesa: 2013
Autor(a) principal: Gonçalves, Aline de Oliveira [UNESP]
Orientador(a): Não Informado pela instituição
Banca de defesa: Não Informado pela instituição
Tipo de documento: Dissertação
Tipo de acesso: Acesso aberto
Idioma: por
Instituição de defesa: Universidade Estadual Paulista (Unesp)
Programa de Pós-Graduação: Não Informado pela instituição
Departamento: Não Informado pela instituição
País: Não Informado pela instituição
Palavras-chave em Português:
Link de acesso: http://hdl.handle.net/11449/110809
Resumo: This study aims to evaluate the effect of Er: YAG (L) and bur (B) on the strength of resistance microshear (MPa) and the effect on the interface adhesive stickers and wash conditions (CL) - Adper Scotchbond Multipurpose and self (CS) - Adper EasyOne, both from 3M ESPE. Were formed 4 groups according tools and adhesives: B_CL (control); B_CS; L_CL and L_CS. 60 bovine incisors were randomly divided into experimental and groups: 40 to force microshear resistance (n = 10) and 20 for the adhesive interface morphology (6 to measure the thickness of the hybrid layer (CH) and length of tags (t) by MLCF (n = 3); 12 to the adhesive interface morphology by SEM (n = 3) and 2 to illustrate the effect of the instruments on dentine by SEM (n = 1). Microshear For testing four cylinders were fabricated composite Filtek Z350 XT - 3M ESPE (0.7 mm in diameter and 1 mm in height and area of adhesion of 0.38 mm) on each dentin surface treated by tools and adhesives. Testing of bond strength was performed in microshear FDMS universal testing machine 2000 with a load cell of 500 kgf and a speed of 0.5 mm / min. Adhesive interface was characterized by layer thickness hybrid (HC) and length of tags (t) in nm, with software UTHSCSA ImageTool. Values of bond strength to microshear L_CL were 34.10 ± 19.07, 24.26 ± 9.35 B_CL, L_CN 33.18 ± 12.46, 21.24 ± 13.96 B_CN. Anova two- way resulted in statistically significant only for instruments (p = 0.047). Mann-Whitney identified instruments to determine significant differences CH thickness and length (t). adhesives for these differences were only observed for (t). It can be concluded that 1) Laser Er: YAG results in higher bond strength to the microshear, regardless of the adhesive system (CL and CS). 2) The tags have no significant effect on bond strength to microshear. 3) The adhesive interface is affected by both instruments for cavity preparation and the type of adhesive system...