Síntese e caracterização de peneiras moleculares mesoporosas do tipo MCM-41 e AlMCM-41 a partir de fontes alternativas de sílica e de alumínio

• Ano de defesa: 2009
• Autor(a) principal: Silva, Marta Lígia Pereira da
• Orientador(a): Melo, Dulce Maria de Araújo
• Tipo de documento: Tese
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: Universidade Federal do Rio Grande do Norte
• Programa de Pós-Graduação: Programa de Pós-Graduação em Ciência e Engenharia de Materiais
• Departamento: Processamento de Materiais a partir do Pó; Polímeros e Compósitos; Processamento de Materiais a part
• País: BR
• Palavras-chave em Português: Síntese hidrotérmica; MCM-41; AlMCM-41; Quartzo e aluminosilicato
• Palavras-chave em Inglês: Hidrotérmico synthesis; MCM-41; AlMCM-41; Quartz and aluminosilicate mineral
• Área do conhecimento CNPq: CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
• Link de acesso: https://repositorio.ufrn.br/jspui/handle/123456789/12736

The mesoporous molecular sieves of MCM-41 and AlMCM-41 type are considered as promising support for metal in the refining processes of petroleum-based materials as catalysts and adsorbents for environmental protection. In this work the molecular sieves MCM-41 and AlMCM-41 were synthesized by replacing the source of silica conventionally used, for quartz, an alternative and abundant, and the use of waste from the production of diatomaceous earth, an aluminum-silicate, as a source aluminum, due to abundant reserves of diatomaceous earth in the state of Rio Grande do Norte in the city of Ceará-Mirim, with the objective of producing high-value materials that have similar characteristics to traditional commercial catalysts in the market. These materials were synthesized by the method of hydrothermal synthesis at 100 º C for 7 days and subjected to calcination at 500 º C for 2 hours under flow of nitrogen and air. The molecular sieves were characterized by X-ray diffraction (XRD), differential thermal analysis (DTA) and thermogravimetric analysis (TG), adsorption of N2 (BET and BJH methods), spectroscopy in the infra red (FTIR), microscopy scanning electron (SEM) and transmission electron microscopy (TEM). The analysis indicated that the synthesized materials showed characteristic hexagonal structure of mesopores materials with high specific surface area and sort and narrow distribution of size of pores