CORRELAÇÕES MORFOLÓGICAS ESTRUTURAIS: UM ESTUDO DAS PROPRIEDADES DE VIDROS TELURETOS DO SISTEMA TeO2 - Li2O - MoO3 EM FUNÇÃO DA COMPOSIÇÃO

• Ano de defesa: 2015
• Autor(a) principal: Gomes Junior, João Luiz
• Orientador(a): Novatski, Andressa
• Banca de defesa: Astrath, Nelson Guilherme Castelli , Szezech Júnior, José Danilo
• Tipo de documento: Dissertação
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: UNIVERSIDADE ESTADUAL DE PONTA GROSSA
• Programa de Pós-Graduação: Programa de Pós-Graduação em Ciências
• Departamento: Fisica
• País: BR
• Palavras-chave em Português: vidros tluretos; oxigênios não ligados; energia de Band Gap; basicidade óptica
• Palavras-chave em Inglês: tellurite glasses; non-bridging oxygen; energy Band Gap; optical basicity
• Área do conhecimento CNPq: CNPQ::CIENCIAS EXATAS E DA TERRA::FISICA
• Link de acesso: http://tede2.uepg.br/jspui/handle/prefix/841

In this work, the correlation between the structural morphology with thermal, optical and mechanical properties of (1 – x – y)TeO2-xLi2O-yMoO3 glasses was studied. The analysis was divided into three sets of samples, varying according to the composition for technique. The results reveal different behaviors for each set vitreous stabilities. The Raman spectroscopy and FTIR results showed a similar structural change between each set with decrease NBOs and new peaks position. The Raman and FTIR spectra results showed that with increasing content x and y, concomitantly, occur the conversion of TeO4 to TeO3+1 units, then, in addition to TeO3 units. Furthermore occurs change coordination in the structural units Mo atoms 4 to 6 and these structural changes. Li addition causes these structural changes. This fact confirmed by the Band Gap energy values, which increase with the increase of x and y, it decreases the optical basicity and refractive index values. By optical absorption measurements determined the Band Gap energy values of all samples. It was concluded that occur direct transitions allowed in all sets. The behavior of increasing Band Gap values and decreasing Optical basicity confirmed the decreasing in the NBO content leading to an indication of a more polymerized network for a variation of x mol%. Finally the behaviors elastic modulus and hardness, which shows decreased stiffness of the material with the incorporation of Li2O and MoO3 concomitantly, is presented. x