Detalhes bibliográficos
| Ano de defesa: |
2015 |
| Autor(a) principal: |
Mildner, Mariele Diná
 |
| Orientador(a): |
Oshima, Hugo Mitsuo Silva
|
| Banca de defesa: |
Não Informado pela instituição |
| Tipo de documento: |
Dissertação
|
| Tipo de acesso: |
Acesso aberto |
| Idioma: |
por |
| Instituição de defesa: |
Pontifícia Universidade Católica do Rio Grande do Sul
|
| Programa de Pós-Graduação: |
Programa de Pós-Graduação em Odontologia
|
| Departamento: |
Faculdade de Odontologia
|
| País: |
Brasil
|
| Palavras-chave em Português: |
|
| Área do conhecimento CNPq: |
|
| Link de acesso: |
http://tede2.pucrs.br/tede2/handle/tede/6298
|
Resumo: |
An appropriate monomer conversion of composite resins is very important to improve your biocompatibility. The aim of this study was to evaluate additional polymerization methods of dental resins cytotoxicity. A total of 72 samples were prepared from the following materials: Filtek Z350XT® (3M/ESPE, St Paul, MN, EUA), Sinfony (3M/ESPE, St Paul, MN, EUA), Lava Ultimate (3M/ESPE, St Paul, MN, EUA). The used color was A2 for all composite resins. To Filtek Z350XT and Sinfony a Teflon mould (3x2mm) was used. From Lava Ultimate block 1,6mm cubes was cutting with diamond discs and digital pachymeter. Samples was divided in 4 groups: FK Group: 20s LED polymerization, S Group: Sinfony with light and vacuum additional polymerization, L Group: Lava Ultimate, FPA Group: Filtek Z350XT with light and vacuum additional polymerization. Evaluate specimens was stored in DMEM medium for 24, 48 and 72 hours respectively. Thereafter, culture medium was in contact with NIH/3T3 fibroblasts. MTT test determined cellular viability. Statistical analysis realized by Levene and Kolmogorov-Smirnov tests (α=0,05). The S group show the lower cytotoxicity. Additional polymerization of FK group wasn´t efficient to cellular viability. Sinfony presented minor cytotoxicity among all tested materials. Light and vacuum additional polymerization of Filtek Z350XT don´t improve your cytotoxicity results when compared with direct polymerization of the same dental composite. |