Influência da espessura e grau de translucidez dos materiais nanocerâmicos utilizados em CAD/CAM e do tipo de cimento na cor final de facetas

• Ano de defesa: 2016
• Autor(a) principal: Peixoto, Maurício Tomazoni
• Orientador(a): Mota, Eduardo Gonçalves
• Tipo de documento: Dissertação
• Tipo de acesso: Acesso aberto
• Idioma: por
• Instituição de defesa: Pontifícia Universidade Católica do Rio Grande do Sul
• Programa de Pós-Graduação: Programa de Pós-Graduação em Odontologia
• Departamento: Faculdade de Odontologia
• País: Brasil
• Palavras-chave em Português: Facetas; Alteração de Cor; CAD/CAM
• Área do conhecimento CNPq: CIENCIAS DA SAUDE::ODONTOLOGIA
• Link de acesso: http://tede2.pucrs.br/tede2/handle/tede/7297

The increasing demand for aesthetic restorations, associated with the evolution of techniques and materials, allowed the preparation of prosthetic pieces of reduced thickness. The introduction of CAD / CAM technology has made accurate and fast restorations. However, the final color of the restoration remains the direct responsibility of the dentist, where a visual assessment of color can cause errors, while an instrumental color measurement has accurate readings. The objective of the study was to investigate the factors that may influence the final color and translucency of different veneers with different thicknesses made by CAD/CAM materials and different types of resin cements on a darkened substrate. The samples were made by copy biogeneric in the CEREC SW 4.2 system, after a sample calculation of the pilot project, 60 upper central incisors of the right side of color C3 of epoxy resin were selected in 12 groups of 5 elements, divided according to type of (Lava Ultimate HT and LT), facet thickness (0.3mm / 0.6mm / 1.0mm) and cement type (Relyx Ultimate and Relyx Veneer). After cementation, the samples were taken with the spectrophotometer at a value of ΔE in 6 different times with a silicone guide on the tooth, which ensures that the color is uniform. The results showed a significant difference in the values of ΔE in groups 1 and 4 (HT and LT of 0.3 mm) cemented with Relyx Ultimate, in groups 7 and 9 (HT of 0.3 mm and 1.0 mm), and in groups 10 And 12 (LT of 0.3mm and 1.0mm) cemented with Relyx Veneer. However, the results were not significant for the masking of the darkened substrate over time, however, significant differences in ΔE values were.