Estudo de fadiga em engrenagens di diferencial de veículos elétricos
Guardat en:
| Autor principal: | |
|---|---|
| Data de publicació: | 2025 |
| Format: | Master thesis |
| Idioma: | por |
| Font: | Repositório Institucional da UPF |
| Download full: | https://repositorio.upf.br/handle/123456789/9997 |
Sumari: | This study investigated the fatigue behavior of bevel gears used in electric vehicle differentials, manufactured by the investment casting process from SAE 4320 and DIN 20MnCr5 steels. Four material and heat treatment combinations were evaluated: martempering with tempering and austempering with subzero cooling, both performed after cementation. Characterization involved macro and microstructural analyses by optical and scanning electron microscopy (SEM), microhardness profiles along the cemented layer, and static and sound bending tests on engineering teeth instrumented with strain gauges. The results revealed that martempering conditions presented higher surface hardness, associated with a predominantly martensitic microstructure, in some cases with possible significant fractions of retained austenite, which favored Tooth Flank Initiation Crack (TIFF) failures. On the other hand, the austempering + sub-zero conditions resulted in bainitic microstructures with possible controlled retained austenite, favoring greater energy absorption and a greater number of cycles to fracture. Thus, the austempering + sub-zero treatment, despite presenting lower surface hardness values, demonstrated better fatigue performance and can be recommended for electric vehicle gears subjected to intense cyclic loading. |
| _version_ | 1871607648916340736 |
|---|---|
| author | Santos, Maria Luiza dos |
| author_browse | Santos, Maria Luiza dos |
| author_facet | Santos, Maria Luiza dos |
| author_role | author |
| collection | Repositório Institucional da UPF |
| dc.contributor.author.fl_str_mv | Santos, Maria Luiza dos |
| dc.contributor.none.fl_str_mv | Haupt, William |
| dc.date.none.fl_str_mv | 2025-09-25 2026-02-24T16:25:00Z 2026-02-24 |
| dc.format.none.fl_str_mv | application/pdf |
| dc.identifier.uri.fl_str_mv | SANTOS, Maria Luiza dos. Estudo de fadiga em engrenagens di diferencial de veículos elétricos. 2025. 84 f. Dissertação (Mestrado em Projeto e Processos de Fabricação) -- Universidade de Passo Fundo, 2025. https://repositorio.upf.br/handle/123456789/9997 |
| dc.language.iso.fl_str_mv | por |
| dc.publisher.none.fl_str_mv | Universidade de Passo Fundo Brasil UPF Programa de Pós-Graduação em Projeto e Processos de Fabricação Instituto de Tecnologia |
| dc.rights.driver.fl_str_mv | info:eu-repo/semantics/openAccess |
| dc.source.none.fl_str_mv | reponame:Repositório Institucional da UPF instname:Universidade de Passo Fundo (UPF) instacron:UPF |
| dc.subject.por.fl_str_mv | Engrenagens Veículos elétricos Aço fadiga Aço tratamento térmico Engenharias::Engenharia Mecânica::Processos de Fabricação |
| dc.title.none.fl_str_mv | Estudo de fadiga em engrenagens di diferencial de veículos elétricos |
| dc.type.driver.fl_str_mv | info:eu-repo/semantics/masterThesis |
| dc.type.status.fl_str_mv | info:eu-repo/semantics/publishedVersion |
| description | This study investigated the fatigue behavior of bevel gears used in electric vehicle differentials, manufactured by the investment casting process from SAE 4320 and DIN 20MnCr5 steels. Four material and heat treatment combinations were evaluated: martempering with tempering and austempering with subzero cooling, both performed after cementation. Characterization involved macro and microstructural analyses by optical and scanning electron microscopy (SEM), microhardness profiles along the cemented layer, and static and sound bending tests on engineering teeth instrumented with strain gauges. The results revealed that martempering conditions presented higher surface hardness, associated with a predominantly martensitic microstructure, in some cases with possible significant fractions of retained austenite, which favored Tooth Flank Initiation Crack (TIFF) failures. On the other hand, the austempering + sub-zero conditions resulted in bainitic microstructures with possible controlled retained austenite, favoring greater energy absorption and a greater number of cycles to fracture. Thus, the austempering + sub-zero treatment, despite presenting lower surface hardness values, demonstrated better fatigue performance and can be recommended for electric vehicle gears subjected to intense cyclic loading. |
| eu_rights_str_mv | openAccess |
| format | masterThesis |
| id | UPF_f2192d11bc65f9e1618b06e8ed44a5f7 |
| identifier_str_mv | SANTOS, Maria Luiza dos. Estudo de fadiga em engrenagens di diferencial de veículos elétricos. 2025. 84 f. Dissertação (Mestrado em Projeto e Processos de Fabricação) -- Universidade de Passo Fundo, 2025. |
| instacron_str | UPF |
| institution | UPF |
| instname_str | Universidade de Passo Fundo (UPF) |
| language | por |
| network_acronym_str | UPF |
| network_name_str | Repositório Institucional da UPF |
| oai_identifier_str | oai:repositorio.upf.br:123456789/9997 |
| publishDate | 2025 |
| publishDateSort | 2025 |
| publisher.none.fl_str_mv | Universidade de Passo Fundo Brasil UPF Programa de Pós-Graduação em Projeto e Processos de Fabricação Instituto de Tecnologia |
| reponame_str | Repositório Institucional da UPF |
| repository.mail.fl_str_mv | jucelei@upf.br||biblio@upf.br |
| repository.name.fl_str_mv | Repositório Institucional da UPF - Universidade de Passo Fundo (UPF) |
| repository_id_str | 1610 |
| spelling | Estudo de fadiga em engrenagens di diferencial de veículos elétricosEngrenagensVeículos elétricosAço fadigaAço tratamento térmicoEngenharias::Engenharia Mecânica::Processos de FabricaçãoThis study investigated the fatigue behavior of bevel gears used in electric vehicle differentials, manufactured by the investment casting process from SAE 4320 and DIN 20MnCr5 steels. Four material and heat treatment combinations were evaluated: martempering with tempering and austempering with subzero cooling, both performed after cementation. Characterization involved macro and microstructural analyses by optical and scanning electron microscopy (SEM), microhardness profiles along the cemented layer, and static and sound bending tests on engineering teeth instrumented with strain gauges. The results revealed that martempering conditions presented higher surface hardness, associated with a predominantly martensitic microstructure, in some cases with possible significant fractions of retained austenite, which favored Tooth Flank Initiation Crack (TIFF) failures. On the other hand, the austempering + sub-zero conditions resulted in bainitic microstructures with possible controlled retained austenite, favoring greater energy absorption and a greater number of cycles to fracture. Thus, the austempering + sub-zero treatment, despite presenting lower surface hardness values, demonstrated better fatigue performance and can be recommended for electric vehicle gears subjected to intense cyclic loading.Este trabalho investigou o comportamento em fadiga de engrenagens cônicas utilizadas em diferenciais de veículos elétricos, fabricadas pelo processo de microfusão com posterior cementação superficial a partir dos aços SAE 4320 e DIN 20MnCr5. Foram avaliadas quatro combinações de material e tratamento térmico: martêmpera com revenimento e austêmpera com resfriamento sub-zero, ambos realizados após a cementação. A caracterização envolveu análises macrográficas e microestruturais por estereomicroscópio, microscopia óptica e microscopia eletrônica de varredura (MEV), perfil de microdureza ao longo da camada cementada e ensaios estáticos e dinâmicos de flexão em dentes de engrenagem instrumentados com strain gauges. Os resultados revelaram que as condições martêmpera apresentaram maior dureza superficial, associada a microestrutura predominantemente martensítica, em alguns casos, com possíveis frações significativas de austenita retida, o que favoreceu falhas do tipo Trinca de Iniciação no Flanco do Dente (TIFF). Por outro lado, as condições austêmpera + sub- zero resultaram em microestruturas bainíticas com possível presença de austenita retida controlada, favorecendo maior absorção de energia e maior número de ciclos até a fratura. Assim, o tratamento austêmpera + sub-zero, apesar de apresentar menores valores de dureza superficial, demonstrou melhor desempenho em fadiga, podendo ser recomendado para engrenagens de veículos elétricos submetidas a carregamentos cíclicos intensos.Universidade de Passo FundoBrasilUPFPrograma de Pós-Graduação em Projeto e Processos de FabricaçãoInstituto de TecnologiaHaupt, WilliamSantos, Maria Luiza dos2026-02-24T16:25:00Z2026-02-242025-09-25info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfSANTOS, Maria Luiza dos. Estudo de fadiga em engrenagens di diferencial de veículos elétricos. 2025. 84 f. Dissertação (Mestrado em Projeto e Processos de Fabricação) -- Universidade de Passo Fundo, 2025.https://repositorio.upf.br/handle/123456789/9997porinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UPFinstname:Universidade de Passo Fundo (UPF)instacron:UPF2026-02-25T03:01:49Zoai:repositorio.upf.br:123456789/9997Repositório InstitucionalPRIhttp://repositorio.upf.br/oai/requestjucelei@upf.br||biblio@upf.bropendoar:16102026-02-25T03:01:49Repositório Institucional da UPF - Universidade de Passo Fundo (UPF) |
| spellingShingle | Estudo de fadiga em engrenagens di diferencial de veículos elétricos Santos, Maria Luiza dos Engrenagens Veículos elétricos Aço fadiga Aço tratamento térmico Engenharias::Engenharia Mecânica::Processos de Fabricação |
| status_str | publishedVersion |
| title | Estudo de fadiga em engrenagens di diferencial de veículos elétricos |
| title_full | Estudo de fadiga em engrenagens di diferencial de veículos elétricos |
| title_fullStr | Estudo de fadiga em engrenagens di diferencial de veículos elétricos |
| title_full_unstemmed | Estudo de fadiga em engrenagens di diferencial de veículos elétricos |
| title_short | Estudo de fadiga em engrenagens di diferencial de veículos elétricos |
| title_sort | Estudo de fadiga em engrenagens di diferencial de veículos elétricos |
| topic | Engrenagens Veículos elétricos Aço fadiga Aço tratamento térmico Engenharias::Engenharia Mecânica::Processos de Fabricação |
| url | https://repositorio.upf.br/handle/123456789/9997 |