Resistência à flexão de diferentes sistemas de pinos de fibra de vidro personalizados
Furkejuvvon:
| Váldodahkki: | |
|---|---|
| Almmustuhttinbeaivi: | 2021 |
| Materiálatiipa: | Bachelor thesis |
| Giella: | por |
| Gáldu: | Repositório Institucional da UPF |
| Download full: | https://repositorio.upf.br/handle/123456789/7405 |
Čoahkkáigeassu: | The objective of this work was to compare the flexural strength of conventional fiberglass posts relined with composite resin to custom adjustable posts and single-body fiberglass posts milled in CAD-CAM. Thirty specimens (n=10) were made with the following retainers: (1) PCM - prefabricated fiberglass posts (Exact no. 2 - Angelus®, Londrina, PR, Brazil) relined with composite resin; (2) PFF - pins milled in CAD-CAM from a Fibercad wafer (Fibercad - Angelus®, Londrina, PR, Brazil); and (3) PPA -adjustable custom pins (Splendor SAP - Angelus®, Londrina, PR, Brazil). The specimens were submitted to the three-point bending test, in a universal testing machine, with a load cell of 2,000 N, which focused its force on the center of the specimens, at a speed of 0.05 mm /min. Mean resistance values were compared between groups, using the 1-factor Anova and Tukey tests, at a significance level of 95%. The results showed that the PFF group presented a superior flexural resistance to the PPA and PCM groups (p=0.000). The PPA and PCM groups did not show statistical differences between them. In conclusion, the pins milled in CAD-CAM (PFF) are the ones that most resist a flexural force among the three materials tested in the experiment. |
| _version_ | 1871607639420436480 |
|---|---|
| author | Dutra, Mateus José |
| author_browse | Dutra, Mateus José |
| author_facet | Dutra, Mateus José |
| author_role | author |
| collection | Repositório Institucional da UPF |
| dc.contributor.author.fl_str_mv | Dutra, Mateus José |
| dc.contributor.none.fl_str_mv | Corazza, Pedro Henrique |
| dc.date.none.fl_str_mv | 2021-11-17 2025-05-10T22:22:36Z |
| dc.format.none.fl_str_mv | application/pdf |
| dc.identifier.uri.fl_str_mv | DUTRA, Mateus José. Resistência à flexão de diferentes sistemas de pinos de fibra de vidro personalizados. 2021. 56 f. Trabalho de Conclusão de Curso (Cirurgião-dentista). Curso de Odontologia. Universidade de Passo Fundo, Passo Fundo, 2021. https://repositorio.upf.br/handle/123456789/7405 |
| dc.language.iso.fl_str_mv | por |
| dc.publisher.none.fl_str_mv | Universidade de Passo Fundo Faculdade de Odontologia - FO Brasil UPF |
| dc.rights.driver.fl_str_mv | info:eu-repo/semantics/openAccess |
| dc.source.none.fl_str_mv | reponame:Repositório Institucional da UPF instname:Universidade de Passo Fundo (UPF) instacron:UPF |
| dc.subject.por.fl_str_mv | Odontologia Materiais dentários Desenho assistido por computador Resistência à flexão Pinos dentários |
| dc.title.none.fl_str_mv | Resistência à flexão de diferentes sistemas de pinos de fibra de vidro personalizados |
| dc.type.driver.fl_str_mv | info:eu-repo/semantics/bachelorThesis |
| dc.type.status.fl_str_mv | info:eu-repo/semantics/publishedVersion |
| description | The objective of this work was to compare the flexural strength of conventional fiberglass posts relined with composite resin to custom adjustable posts and single-body fiberglass posts milled in CAD-CAM. Thirty specimens (n=10) were made with the following retainers: (1) PCM - prefabricated fiberglass posts (Exact no. 2 - Angelus®, Londrina, PR, Brazil) relined with composite resin; (2) PFF - pins milled in CAD-CAM from a Fibercad wafer (Fibercad - Angelus®, Londrina, PR, Brazil); and (3) PPA -adjustable custom pins (Splendor SAP - Angelus®, Londrina, PR, Brazil). The specimens were submitted to the three-point bending test, in a universal testing machine, with a load cell of 2,000 N, which focused its force on the center of the specimens, at a speed of 0.05 mm /min. Mean resistance values were compared between groups, using the 1-factor Anova and Tukey tests, at a significance level of 95%. The results showed that the PFF group presented a superior flexural resistance to the PPA and PCM groups (p=0.000). The PPA and PCM groups did not show statistical differences between them. In conclusion, the pins milled in CAD-CAM (PFF) are the ones that most resist a flexural force among the three materials tested in the experiment. |
| eu_rights_str_mv | openAccess |
| format | bachelorThesis |
| id | UPF_a784d34c052b63cff85a47df435bdee7 |
| identifier_str_mv | DUTRA, Mateus José. Resistência à flexão de diferentes sistemas de pinos de fibra de vidro personalizados. 2021. 56 f. Trabalho de Conclusão de Curso (Cirurgião-dentista). Curso de Odontologia. Universidade de Passo Fundo, Passo Fundo, 2021. |
| instacron_str | UPF |
| institution | UPF |
| instname_str | Universidade de Passo Fundo (UPF) |
| language | por |
| network_acronym_str | UPF |
| network_name_str | Repositório Institucional da UPF |
| oai_identifier_str | oai:repositorio.upf.br:123456789/7405 |
| publishDate | 2021 |
| publishDateSort | 2021 |
| publisher.none.fl_str_mv | Universidade de Passo Fundo Faculdade de Odontologia - FO Brasil UPF |
| reponame_str | Repositório Institucional da UPF |
| repository.mail.fl_str_mv | jucelei@upf.br||biblio@upf.br |
| repository.name.fl_str_mv | Repositório Institucional da UPF - Universidade de Passo Fundo (UPF) |
| repository_id_str | 1610 |
| spelling | Resistência à flexão de diferentes sistemas de pinos de fibra de vidro personalizadosOdontologiaMateriais dentáriosDesenho assistido por computadorResistência à flexãoPinos dentáriosThe objective of this work was to compare the flexural strength of conventional fiberglass posts relined with composite resin to custom adjustable posts and single-body fiberglass posts milled in CAD-CAM. Thirty specimens (n=10) were made with the following retainers: (1) PCM - prefabricated fiberglass posts (Exact no. 2 - Angelus®, Londrina, PR, Brazil) relined with composite resin; (2) PFF - pins milled in CAD-CAM from a Fibercad wafer (Fibercad - Angelus®, Londrina, PR, Brazil); and (3) PPA -adjustable custom pins (Splendor SAP - Angelus®, Londrina, PR, Brazil). The specimens were submitted to the three-point bending test, in a universal testing machine, with a load cell of 2,000 N, which focused its force on the center of the specimens, at a speed of 0.05 mm /min. Mean resistance values were compared between groups, using the 1-factor Anova and Tukey tests, at a significance level of 95%. The results showed that the PFF group presented a superior flexural resistance to the PPA and PCM groups (p=0.000). The PPA and PCM groups did not show statistical differences between them. In conclusion, the pins milled in CAD-CAM (PFF) are the ones that most resist a flexural force among the three materials tested in the experiment.O objetivo deste trabalho foi comparar a resistência à flexão de pinos de fibra de vidro convencionais reembasados com resina composta a pinos personalizados ajustáveis e de pinos de fibra de vidro de corpo único, fresados em CAD-CAM. Foram confeccionados 30 corpos de prova (n=10) com os seguintes retentores: (1) PCM - pinos de fibra de vidro pré fabricados (Exacto no 2 - Angelus®, Londrina, PR, Brasil) reembasados com resina composta; (2) PFF - pinos fresados em CAD-CAM a partir de uma bolacha de Fibercad (Fibercad - Angelus®, Londrina, PR, Brasil); e (3) PPA -pinos personalizados ajustáveis (Splendor SAP - Angelus®, Londrina, PR, Brasil). Os corpos de prova foram submetidos ao teste de flexão por três pontos, em uma máquina de ensaios universal, com uma célula de carga de 2.000 N, que incidiu a sua força no centro dos corpos de prova, à uma velocidade de 0,05 mm/min. Os valores médios de resistência foram comparados entre os grupos, através dos testes Anova 1-fator e Tukey, ao nível de significância de 95%. Os resultados mostraram que o grupo PFF apresentou uma resistência flexural superior aos grupos PPA e PCM (p=0,000). Os grupos PPA e PCM não apresentaram diferenças estatísticas entre si. Como conclusão, os pinos fresados em CAD-CAM (PFF) são os que mais resistem à uma força flexural entre os três materiais testados no experimento.Universidade de Passo FundoFaculdade de Odontologia - FOBrasilUPFCorazza, Pedro HenriqueDutra, Mateus José2025-05-10T22:22:36Z2021-11-17info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/bachelorThesisapplication/pdfDUTRA, Mateus José. Resistência à flexão de diferentes sistemas de pinos de fibra de vidro personalizados. 2021. 56 f. Trabalho de Conclusão de Curso (Cirurgião-dentista). Curso de Odontologia. Universidade de Passo Fundo, Passo Fundo, 2021.https://repositorio.upf.br/handle/123456789/7405porinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UPFinstname:Universidade de Passo Fundo (UPF)instacron:UPF2025-12-30T20:01:35Zoai:repositorio.upf.br:123456789/7405Repositório InstitucionalPRIhttp://repositorio.upf.br/oai/requestjucelei@upf.br||biblio@upf.bropendoar:16102025-12-30T20:01:35Repositório Institucional da UPF - Universidade de Passo Fundo (UPF) |
| spellingShingle | Resistência à flexão de diferentes sistemas de pinos de fibra de vidro personalizados Dutra, Mateus José Odontologia Materiais dentários Desenho assistido por computador Resistência à flexão Pinos dentários |
| status_str | publishedVersion |
| title | Resistência à flexão de diferentes sistemas de pinos de fibra de vidro personalizados |
| title_full | Resistência à flexão de diferentes sistemas de pinos de fibra de vidro personalizados |
| title_fullStr | Resistência à flexão de diferentes sistemas de pinos de fibra de vidro personalizados |
| title_full_unstemmed | Resistência à flexão de diferentes sistemas de pinos de fibra de vidro personalizados |
| title_short | Resistência à flexão de diferentes sistemas de pinos de fibra de vidro personalizados |
| title_sort | Resistência à flexão de diferentes sistemas de pinos de fibra de vidro personalizados |
| topic | Odontologia Materiais dentários Desenho assistido por computador Resistência à flexão Pinos dentários |
| url | https://repositorio.upf.br/handle/123456789/7405 |