Análise de perfis pultrudados com ênfase em suas uniões
Saved in:
| Main Author: | |
|---|---|
| Publication Date: | 2015 |
| Format: | Master thesis |
| Language: | por |
| Source: | Repositório Institucional da UPF |
| Download full: | https://repositorio.upf.br/handle/123456789/4104 |
Summary: | The Glass Fiber Reinforced Polymer (GFRP) profiles, despite having good mechanical properties, still have in its joints some lacunar aspects, especially with respect to the behavior of these, as well in relation with the procedure ofunion between the profiles, in order to achieve the best preservation of its mechanical properties.Thus, the present study was carried out with the objective of measuring the influence of GFRP profile joints on its mechanical properties, with this, to evaluate the possible substitution ofASTM A36 steel with GFRP profiles in road implement structures, getting, therefore, the reducing of equipment weight. For this, an experimental research was carried out, firstly, by testing the test specimens. As the main results, it can be inferred that, due to the analyzes carried out, the use of GFRP in road implements is promising. However, it should be considered the limitation that it has in relation to the impacts and to the low productivity when compared to the steel. This, because of its manipulation, which allows to infer that its use in the implementation still has much to be improved. Also, it is important to understand that the value that it willadd with the weight reduction, justifies the search for more researches that justify its economic viability, being in charge of the user to measure other production variables. |
| _version_ | 1871607636797947904 |
|---|---|
| author | Tortelli, Ricardo |
| author_browse | Tortelli, Ricardo |
| author_facet | Tortelli, Ricardo |
| author_role | author |
| collection | Repositório Institucional da UPF |
| dc.contributor.author.fl_str_mv | Tortelli, Ricardo |
| dc.contributor.none.fl_str_mv | Guimarães, Vagner Alves http://lattes.cnpq.br/2476665230091155 |
| dc.date.none.fl_str_mv | 2015-01-16 2025-05-07T18:08:31Z |
| dc.format.none.fl_str_mv | application/pdf application/pdf |
| dc.identifier.uri.fl_str_mv | TORTELLI, Ricardo. Análise de perfis pultrudados com ênfase em suas uniões. 2015. 111 f. Dissertação (Mestrado em Projeto e Processos de Fabricação) - Universidade de Passo Fundo, Passo Fundo, RS, 2015. https://repositorio.upf.br/handle/123456789/4104 |
| dc.language.iso.fl_str_mv | por |
| dc.publisher.none.fl_str_mv | Universidade de Passo Fundo Faculdade de Engenharia e Arquitetura – FEAR Brasil UPF Programa de Pós-Graduação em Projeto e Processos de Fabricação |
| dc.rights.driver.fl_str_mv | info:eu-repo/semantics/openAccess |
| dc.source.none.fl_str_mv | reponame:Repositório Institucional da UPF instname:Universidade de Passo Fundo (UPF) instacron:UPF |
| dc.subject.por.fl_str_mv | Processos de fabricação Aço Compósitos poliméricos Tratamento térmico ENGENHARIAS::ENGENHARIA MECANICA |
| dc.title.none.fl_str_mv | Análise de perfis pultrudados com ênfase em suas uniões Analysis of pultruded profiles with emphasis on their joints |
| dc.type.driver.fl_str_mv | info:eu-repo/semantics/masterThesis |
| dc.type.status.fl_str_mv | info:eu-repo/semantics/publishedVersion |
| description | The Glass Fiber Reinforced Polymer (GFRP) profiles, despite having good mechanical properties, still have in its joints some lacunar aspects, especially with respect to the behavior of these, as well in relation with the procedure ofunion between the profiles, in order to achieve the best preservation of its mechanical properties.Thus, the present study was carried out with the objective of measuring the influence of GFRP profile joints on its mechanical properties, with this, to evaluate the possible substitution ofASTM A36 steel with GFRP profiles in road implement structures, getting, therefore, the reducing of equipment weight. For this, an experimental research was carried out, firstly, by testing the test specimens. As the main results, it can be inferred that, due to the analyzes carried out, the use of GFRP in road implements is promising. However, it should be considered the limitation that it has in relation to the impacts and to the low productivity when compared to the steel. This, because of its manipulation, which allows to infer that its use in the implementation still has much to be improved. Also, it is important to understand that the value that it willadd with the weight reduction, justifies the search for more researches that justify its economic viability, being in charge of the user to measure other production variables. |
| eu_rights_str_mv | openAccess |
| format | masterThesis |
| id | UPF_8eb006e4c90ff89a1bf5264e8d2510ea |
| identifier_str_mv | TORTELLI, Ricardo. Análise de perfis pultrudados com ênfase em suas uniões. 2015. 111 f. Dissertação (Mestrado em Projeto e Processos de Fabricação) - Universidade de Passo Fundo, Passo Fundo, RS, 2015. |
| instacron_str | UPF |
| institution | UPF |
| instname_str | Universidade de Passo Fundo (UPF) |
| language | por |
| network_acronym_str | UPF |
| network_name_str | Repositório Institucional da UPF |
| oai_identifier_str | oai:repositorio.upf.br:123456789/4104 |
| publishDate | 2015 |
| publishDateSort | 2015 |
| publisher.none.fl_str_mv | Universidade de Passo Fundo Faculdade de Engenharia e Arquitetura – FEAR Brasil UPF Programa de Pós-Graduação em Projeto e Processos de Fabricação |
| reponame_str | Repositório Institucional da UPF |
| repository.mail.fl_str_mv | jucelei@upf.br||biblio@upf.br |
| repository.name.fl_str_mv | Repositório Institucional da UPF - Universidade de Passo Fundo (UPF) |
| repository_id_str | 1610 |
| spelling | Análise de perfis pultrudados com ênfase em suas uniõesAnalysis of pultruded profiles with emphasis on their jointsProcessos de fabricaçãoAçoCompósitos poliméricosTratamento térmicoENGENHARIAS::ENGENHARIA MECANICAThe Glass Fiber Reinforced Polymer (GFRP) profiles, despite having good mechanical properties, still have in its joints some lacunar aspects, especially with respect to the behavior of these, as well in relation with the procedure ofunion between the profiles, in order to achieve the best preservation of its mechanical properties.Thus, the present study was carried out with the objective of measuring the influence of GFRP profile joints on its mechanical properties, with this, to evaluate the possible substitution ofASTM A36 steel with GFRP profiles in road implement structures, getting, therefore, the reducing of equipment weight. For this, an experimental research was carried out, firstly, by testing the test specimens. As the main results, it can be inferred that, due to the analyzes carried out, the use of GFRP in road implements is promising. However, it should be considered the limitation that it has in relation to the impacts and to the low productivity when compared to the steel. This, because of its manipulation, which allows to infer that its use in the implementation still has much to be improved. Also, it is important to understand that the value that it willadd with the weight reduction, justifies the search for more researches that justify its economic viability, being in charge of the user to measure other production variables.Os perfis de Glass Fiber Reinforced Polymer (GFRP), apesar de possuírem boas propriedades mecânicas, ainda possuem em suas uniões alguns aspectos lacunares, especialmente no que tange ao comportamento dessas, bem como em relação ao procedimento de união entre os perfis, de forma a alcançar a melhor preservação de suas propriedades mecânicas. Assim considerado, o presente estudo se deu com o objetivo de mensurar a influência das uniões de perfis de GFRP em suas propriedades mecânicas para, com isso, avaliar a possível substituição de aço ASTM A36 por perfis de GFRP em estruturas de implementos rodoviários, obtendo-se, assim, a redução do peso dos equipamentos. Para tanto realizou-se uma pesquisa experimental, primeiramente, testando-se corpos de prova. Como principais resultados pode-se inferir que, em virtude das análises realizadas, a utilização do GFRP em implementos rodoviários se mostra promissora. Contudo deve-se considerar a limitação que o mesmo possui em relação aos impactos e à baixa produtividade quando comparado ao aço. Isso, devido à sua manipulação, o que permite inferir que sua utilização na implementação ainda tem muito a ser melhorada. Ainda, importa compreender que o valor que o mesmo agregará com a redução de peso, justifica a busca por mais pesquisas que justifiquem sua viabilidade econômica, ficando a cargo de seu utilizador mensurar outras variáveis de produção.Universidade de Passo FundoFaculdade de Engenharia e Arquitetura – FEARBrasilUPFPrograma de Pós-Graduação em Projeto e Processos de FabricaçãoGuimarães, Vagner Alveshttp://lattes.cnpq.br/2476665230091155Tortelli, Ricardo2025-05-07T18:08:31Z2015-01-16info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfapplication/pdfTORTELLI, Ricardo. Análise de perfis pultrudados com ênfase em suas uniões. 2015. 111 f. Dissertação (Mestrado em Projeto e Processos de Fabricação) - Universidade de Passo Fundo, Passo Fundo, RS, 2015.https://repositorio.upf.br/handle/123456789/4104porinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UPFinstname:Universidade de Passo Fundo (UPF)instacron:UPF2025-12-30T19:46:13Zoai:repositorio.upf.br:123456789/4104Repositório InstitucionalPRIhttp://repositorio.upf.br/oai/requestjucelei@upf.br||biblio@upf.bropendoar:16102025-12-30T19:46:13Repositório Institucional da UPF - Universidade de Passo Fundo (UPF) |
| spellingShingle | Análise de perfis pultrudados com ênfase em suas uniões Tortelli, Ricardo Processos de fabricação Aço Compósitos poliméricos Tratamento térmico ENGENHARIAS::ENGENHARIA MECANICA |
| status_str | publishedVersion |
| title | Análise de perfis pultrudados com ênfase em suas uniões |
| title_full | Análise de perfis pultrudados com ênfase em suas uniões |
| title_fullStr | Análise de perfis pultrudados com ênfase em suas uniões |
| title_full_unstemmed | Análise de perfis pultrudados com ênfase em suas uniões |
| title_short | Análise de perfis pultrudados com ênfase em suas uniões |
| title_sort | Análise de perfis pultrudados com ênfase em suas uniões |
| topic | Processos de fabricação Aço Compósitos poliméricos Tratamento térmico ENGENHARIAS::ENGENHARIA MECANICA |
| url | https://repositorio.upf.br/handle/123456789/4104 |