Efeito da mesogeometria da broca e das condições de lubrirrefrigeração sobre o acabamento em aço DIN S700MC
Uloženo v:
| Hlavní autor: | |
|---|---|
| Datum vydání: | 2016 |
| Médium: | Master thesis |
| Jazyk: | por |
| Zdroj: | Repositório Institucional da UPF |
| Download full: | https://repositorio.upf.br/handle/123456789/4109 |
Shrnutí: | This study presents an investigation on the behavior and effect of the machining process by drilling through a DIN S700MC steel alloy, correlating the preparation of cutting edge geometrywith different cooling-lubrication conditions, and focusing on the surface finishing of the machined part. In this context, experimental tests were performed with different coolinglubrication systems (abundance, MQL, and dry) using solid carbide twist drills, coated with titanium aluminum nitride, with or without meso-geometry preparation (roundings). As response variables, the texture (roughness), the layer affected by heat throughout the hole, and microhardness and burr dimensional profiles were assessed. The results indicate a significant reduction of roughness values when using the rounding drill flank, face and guides. Statistically, this result was not influenced by the different cooling-lubrication. Regarding burr dimension generated by the process, the tool with no meso-geometry preparation presented the same values along with the application of fluid in abundance (emulsion). In the analysis of the layer affected by heat, the tool with meso-geometry preparation presented lower values of the affected layer (microstructure change) and, statistically, there were no significant variations between the application of fluid in abundance and with minimum quantity of lubricant. In the evaluation of microhardness profile, there was no clear conclusion about the influence of thermal and mechanical requirements on the region close to the hole edge, because of the effect of edge deformation caused by microindentation. |
| _version_ | 1871607620661411840 |
|---|---|
| author | Silva, Luiz Eduardo da |
| author_browse | Silva, Luiz Eduardo da |
| author_facet | Silva, Luiz Eduardo da |
| author_role | author |
| collection | Repositório Institucional da UPF |
| dc.contributor.author.fl_str_mv | Silva, Luiz Eduardo da |
| dc.contributor.none.fl_str_mv | Consalter, Luiz Airton 20496729004 |
| dc.date.none.fl_str_mv | 2016-07-08 2025-05-07T18:08:32Z |
| dc.format.none.fl_str_mv | application/pdf application/pdf |
| dc.identifier.uri.fl_str_mv | SILVA, Luiz Eduardo da. Efeito da mesogeometria da broca e das condições de lubrirrefrigeração sobre o acabamento em aço DIN S700MC. 2016. 109 f. Dissertação (Mestrado em Projeto e Processos de Fabricação) - Universidade de Passo Fundo, Passo Fundo, RS, 2016. https://repositorio.upf.br/handle/123456789/4109 |
| dc.language.iso.fl_str_mv | por |
| dc.publisher.none.fl_str_mv | Universidade de Passo Fundo Faculdade de Engenharia e Arquitetura – FEAR Brasil UPF Programa de Pós-Graduação em Projeto e Processos de Fabricação |
| dc.rights.driver.fl_str_mv | info:eu-repo/semantics/openAccess |
| dc.source.none.fl_str_mv | reponame:Repositório Institucional da UPF instname:Universidade de Passo Fundo (UPF) instacron:UPF |
| dc.subject.por.fl_str_mv | Processos de fabricação Revestimentos Brocas Metais Corte ENGENHARIAS::ENGENHARIA MECANICA |
| dc.title.none.fl_str_mv | Efeito da mesogeometria da broca e das condições de lubrirrefrigeração sobre o acabamento em aço DIN S700MC Effect of drill mesogeometry and cooling lubrication conditions on the DIN S700MC steel finish |
| dc.type.driver.fl_str_mv | info:eu-repo/semantics/masterThesis |
| dc.type.status.fl_str_mv | info:eu-repo/semantics/publishedVersion |
| description | This study presents an investigation on the behavior and effect of the machining process by drilling through a DIN S700MC steel alloy, correlating the preparation of cutting edge geometrywith different cooling-lubrication conditions, and focusing on the surface finishing of the machined part. In this context, experimental tests were performed with different coolinglubrication systems (abundance, MQL, and dry) using solid carbide twist drills, coated with titanium aluminum nitride, with or without meso-geometry preparation (roundings). As response variables, the texture (roughness), the layer affected by heat throughout the hole, and microhardness and burr dimensional profiles were assessed. The results indicate a significant reduction of roughness values when using the rounding drill flank, face and guides. Statistically, this result was not influenced by the different cooling-lubrication. Regarding burr dimension generated by the process, the tool with no meso-geometry preparation presented the same values along with the application of fluid in abundance (emulsion). In the analysis of the layer affected by heat, the tool with meso-geometry preparation presented lower values of the affected layer (microstructure change) and, statistically, there were no significant variations between the application of fluid in abundance and with minimum quantity of lubricant. In the evaluation of microhardness profile, there was no clear conclusion about the influence of thermal and mechanical requirements on the region close to the hole edge, because of the effect of edge deformation caused by microindentation. |
| eu_rights_str_mv | openAccess |
| format | masterThesis |
| id | UPF_3feb02e7e7bed5fed50a4378e60c1df3 |
| identifier_str_mv | SILVA, Luiz Eduardo da. Efeito da mesogeometria da broca e das condições de lubrirrefrigeração sobre o acabamento em aço DIN S700MC. 2016. 109 f. Dissertação (Mestrado em Projeto e Processos de Fabricação) - Universidade de Passo Fundo, Passo Fundo, RS, 2016. |
| instacron_str | UPF |
| institution | UPF |
| instname_str | Universidade de Passo Fundo (UPF) |
| language | por |
| network_acronym_str | UPF |
| network_name_str | Repositório Institucional da UPF |
| oai_identifier_str | oai:repositorio.upf.br:123456789/4109 |
| publishDate | 2016 |
| publishDateSort | 2016 |
| publisher.none.fl_str_mv | Universidade de Passo Fundo Faculdade de Engenharia e Arquitetura – FEAR Brasil UPF Programa de Pós-Graduação em Projeto e Processos de Fabricação |
| reponame_str | Repositório Institucional da UPF |
| repository.mail.fl_str_mv | jucelei@upf.br||biblio@upf.br |
| repository.name.fl_str_mv | Repositório Institucional da UPF - Universidade de Passo Fundo (UPF) |
| repository_id_str | 1610 |
| spelling | Efeito da mesogeometria da broca e das condições de lubrirrefrigeração sobre o acabamento em aço DIN S700MCEffect of drill mesogeometry and cooling lubrication conditions on the DIN S700MC steel finishProcessos de fabricaçãoRevestimentosBrocasMetaisCorteENGENHARIAS::ENGENHARIA MECANICAThis study presents an investigation on the behavior and effect of the machining process by drilling through a DIN S700MC steel alloy, correlating the preparation of cutting edge geometrywith different cooling-lubrication conditions, and focusing on the surface finishing of the machined part. In this context, experimental tests were performed with different coolinglubrication systems (abundance, MQL, and dry) using solid carbide twist drills, coated with titanium aluminum nitride, with or without meso-geometry preparation (roundings). As response variables, the texture (roughness), the layer affected by heat throughout the hole, and microhardness and burr dimensional profiles were assessed. The results indicate a significant reduction of roughness values when using the rounding drill flank, face and guides. Statistically, this result was not influenced by the different cooling-lubrication. Regarding burr dimension generated by the process, the tool with no meso-geometry preparation presented the same values along with the application of fluid in abundance (emulsion). In the analysis of the layer affected by heat, the tool with meso-geometry preparation presented lower values of the affected layer (microstructure change) and, statistically, there were no significant variations between the application of fluid in abundance and with minimum quantity of lubricant. In the evaluation of microhardness profile, there was no clear conclusion about the influence of thermal and mechanical requirements on the region close to the hole edge, because of the effect of edge deformation caused by microindentation.Este trabalho apresenta uma investigação sobre os comportamentos e os efeitos do processo de usinagem por furação em uma liga DIN S700MC, correlacionando a preparação da geometria do gume com diferentes condições de aplicação de fluídos lubrirrefrigerantes, com foco no acabamento superficial da peça usinada. Neste contexto, foram realizados ensaios experimentais com diferentes sistemas de lubrirrefrigeração (abundância, MQL e a seco), utilizando brocas helicoidais inteiriças de metal-duro, revestidas com nitreto de titânio e alumínio, com e sem preparação da mesogeometria (arredondamentos). Como variáveis de resposta foram avaliados a textura (rugosidade), a camada afetada pelo calor ao longo do furo, o perfil de microdureza e o dimensional da rebarba. Os resultados apontaram para uma redução significativa dos valores de rugosidade com a utilização da broca com arredondamentos no flanco, na face e nas guias. Estatisticamente, este resultado não foi influenciado pelas diferentes condições de aplicação dos fluídos lubrirrefrigerantes. Em relação ao dimensional da rebarba gerada pelo processo, a ferramenta sem preparação da mesogeometria apresentou os menores valores juntamente com a aplicação do Fluído em abundância (emulsão). Na análise da camada afetada pelo calor a ferramenta com preparação da mesogeometria apresentou os menores valores de camada afetada (modificação microestrutural) e estatisticamente não houve variações significativas entre a aplicação do Fluído em abundância e com mínima quantidade de lubrificante. Na avaliação do perfil de microdureza não foi possível uma conclusão clara da influência das solicitações térmicas e mecânicas sobre a região próxima à borda do furo, devido ao efeito de deformação de borda provocada pela microindentação.Universidade de Passo FundoFaculdade de Engenharia e Arquitetura – FEARBrasilUPFPrograma de Pós-Graduação em Projeto e Processos de FabricaçãoConsalter, Luiz Airton20496729004Silva, Luiz Eduardo da2025-05-07T18:08:32Z2016-07-08info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfapplication/pdfSILVA, Luiz Eduardo da. Efeito da mesogeometria da broca e das condições de lubrirrefrigeração sobre o acabamento em aço DIN S700MC. 2016. 109 f. Dissertação (Mestrado em Projeto e Processos de Fabricação) - Universidade de Passo Fundo, Passo Fundo, RS, 2016.https://repositorio.upf.br/handle/123456789/4109porinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UPFinstname:Universidade de Passo Fundo (UPF)instacron:UPF2025-12-30T20:46:08Zoai:repositorio.upf.br:123456789/4109Repositório InstitucionalPRIhttp://repositorio.upf.br/oai/requestjucelei@upf.br||biblio@upf.bropendoar:16102025-12-30T20:46:08Repositório Institucional da UPF - Universidade de Passo Fundo (UPF) |
| spellingShingle | Efeito da mesogeometria da broca e das condições de lubrirrefrigeração sobre o acabamento em aço DIN S700MC Silva, Luiz Eduardo da Processos de fabricação Revestimentos Brocas Metais Corte ENGENHARIAS::ENGENHARIA MECANICA |
| status_str | publishedVersion |
| title | Efeito da mesogeometria da broca e das condições de lubrirrefrigeração sobre o acabamento em aço DIN S700MC |
| title_full | Efeito da mesogeometria da broca e das condições de lubrirrefrigeração sobre o acabamento em aço DIN S700MC |
| title_fullStr | Efeito da mesogeometria da broca e das condições de lubrirrefrigeração sobre o acabamento em aço DIN S700MC |
| title_full_unstemmed | Efeito da mesogeometria da broca e das condições de lubrirrefrigeração sobre o acabamento em aço DIN S700MC |
| title_short | Efeito da mesogeometria da broca e das condições de lubrirrefrigeração sobre o acabamento em aço DIN S700MC |
| title_sort | Efeito da mesogeometria da broca e das condições de lubrirrefrigeração sobre o acabamento em aço DIN S700MC |
| topic | Processos de fabricação Revestimentos Brocas Metais Corte ENGENHARIAS::ENGENHARIA MECANICA |
| url | https://repositorio.upf.br/handle/123456789/4109 |