Influência do hipoclorito de cálcio na resistência de união de materiais restauradores à dentina coronária
Saved in:
| Hovedforfatter: | |
|---|---|
| Publication Date: | 2019 |
| Format: | Bachelor thesis |
| Sprog: | por |
| Source: | Repositório Institucional da UPF |
| Download full: | https://repositorio.upf.br/handle/123456789/7363 |
Summary: | This work aimed to evaluate the influence of Calcium Hypochlorite (Ca(OCl)2) on the bond strength of restorative materials to coronary dentin. For this, 90 bovine mandibular central incisors were used, which were cut in order to expose the dentin of the pulp chamber. The specimens were randomly divided into 9 groups, according to the solution used. Ca(OCl)2 was used as an irrigant at concentrations of 0.5%, 2.5% and 6%, with or without EDTA. Sodium Hypochlorite (NaOCl) was also used at a concentration of 6%. A group with EDTA only and a control group that received no treatment. After being in contact with the substances of the respective groups, the dentin was etched with Phosphoric Acid 37% and Ambar adhesive was used for dentin hybridization. The restoration was performed with composite resin. Each specimen was cut in a metallographic cutter, thus obtaining the “sticks” that passed through a microtensile test. For statistical analysis, the ANOVA test was used followed by the Tukey test. The results show that the control group and the one irrigated only with EDTA were similar (P>0.05); the other groups were similar to each other (P>0.05) and statistically lower than the control group (P>0.05). From the results it can be concluded that NaOCl and Ca(OCl)2, regardless of the concentration used, negatively affect the bond strength of adhesive materials to dentin. |
| _version_ | 1871607618142732288 |
|---|---|
| author | Sala, Letícia |
| author_browse | Sala, Letícia |
| author_facet | Sala, Letícia |
| author_role | author |
| collection | Repositório Institucional da UPF |
| dc.contributor.author.fl_str_mv | Sala, Letícia |
| dc.contributor.none.fl_str_mv | Cecchin, Doglas |
| dc.date.none.fl_str_mv | 2019-10-30 2025-05-10T22:22:25Z |
| dc.format.none.fl_str_mv | application/pdf |
| dc.identifier.uri.fl_str_mv | SALA, Letícia. Influência do hipoclorito de cálcio na resistência de união de materiais restauradores à dentina coronária. 2019. 27 f. Trabalho de Conclusão de Curso (Cirurgião-dentista). Curso de Odontologia. Universidade de Passo Fundo, Passo Fundo, 2019. https://repositorio.upf.br/handle/123456789/7363 |
| dc.language.iso.fl_str_mv | por |
| dc.publisher.none.fl_str_mv | Universidade de Passo Fundo Faculdade de Odontologia - FO Brasil UPF |
| dc.rights.driver.fl_str_mv | info:eu-repo/semantics/openAccess |
| dc.source.none.fl_str_mv | reponame:Repositório Institucional da UPF instname:Universidade de Passo Fundo (UPF) instacron:UPF |
| dc.subject.por.fl_str_mv | Odontologia Dentina Hipoclorito de sódio Hipoclorito de cálcio |
| dc.title.none.fl_str_mv | Influência do hipoclorito de cálcio na resistência de união de materiais restauradores à dentina coronária |
| dc.type.driver.fl_str_mv | info:eu-repo/semantics/bachelorThesis |
| dc.type.status.fl_str_mv | info:eu-repo/semantics/publishedVersion |
| description | This work aimed to evaluate the influence of Calcium Hypochlorite (Ca(OCl)2) on the bond strength of restorative materials to coronary dentin. For this, 90 bovine mandibular central incisors were used, which were cut in order to expose the dentin of the pulp chamber. The specimens were randomly divided into 9 groups, according to the solution used. Ca(OCl)2 was used as an irrigant at concentrations of 0.5%, 2.5% and 6%, with or without EDTA. Sodium Hypochlorite (NaOCl) was also used at a concentration of 6%. A group with EDTA only and a control group that received no treatment. After being in contact with the substances of the respective groups, the dentin was etched with Phosphoric Acid 37% and Ambar adhesive was used for dentin hybridization. The restoration was performed with composite resin. Each specimen was cut in a metallographic cutter, thus obtaining the “sticks” that passed through a microtensile test. For statistical analysis, the ANOVA test was used followed by the Tukey test. The results show that the control group and the one irrigated only with EDTA were similar (P>0.05); the other groups were similar to each other (P>0.05) and statistically lower than the control group (P>0.05). From the results it can be concluded that NaOCl and Ca(OCl)2, regardless of the concentration used, negatively affect the bond strength of adhesive materials to dentin. |
| eu_rights_str_mv | openAccess |
| format | bachelorThesis |
| id | UPF_254f02003c6c19fccb05e4aab7c5b633 |
| identifier_str_mv | SALA, Letícia. Influência do hipoclorito de cálcio na resistência de união de materiais restauradores à dentina coronária. 2019. 27 f. Trabalho de Conclusão de Curso (Cirurgião-dentista). Curso de Odontologia. Universidade de Passo Fundo, Passo Fundo, 2019. |
| instacron_str | UPF |
| institution | UPF |
| instname_str | Universidade de Passo Fundo (UPF) |
| language | por |
| network_acronym_str | UPF |
| network_name_str | Repositório Institucional da UPF |
| oai_identifier_str | oai:repositorio.upf.br:123456789/7363 |
| publishDate | 2019 |
| publishDateSort | 2019 |
| publisher.none.fl_str_mv | Universidade de Passo Fundo Faculdade de Odontologia - FO Brasil UPF |
| reponame_str | Repositório Institucional da UPF |
| repository.mail.fl_str_mv | jucelei@upf.br||biblio@upf.br |
| repository.name.fl_str_mv | Repositório Institucional da UPF - Universidade de Passo Fundo (UPF) |
| repository_id_str | 1610 |
| spelling | Influência do hipoclorito de cálcio na resistência de união de materiais restauradores à dentina coronáriaOdontologiaDentinaHipoclorito de sódioHipoclorito de cálcioThis work aimed to evaluate the influence of Calcium Hypochlorite (Ca(OCl)2) on the bond strength of restorative materials to coronary dentin. For this, 90 bovine mandibular central incisors were used, which were cut in order to expose the dentin of the pulp chamber. The specimens were randomly divided into 9 groups, according to the solution used. Ca(OCl)2 was used as an irrigant at concentrations of 0.5%, 2.5% and 6%, with or without EDTA. Sodium Hypochlorite (NaOCl) was also used at a concentration of 6%. A group with EDTA only and a control group that received no treatment. After being in contact with the substances of the respective groups, the dentin was etched with Phosphoric Acid 37% and Ambar adhesive was used for dentin hybridization. The restoration was performed with composite resin. Each specimen was cut in a metallographic cutter, thus obtaining the “sticks” that passed through a microtensile test. For statistical analysis, the ANOVA test was used followed by the Tukey test. The results show that the control group and the one irrigated only with EDTA were similar (P>0.05); the other groups were similar to each other (P>0.05) and statistically lower than the control group (P>0.05). From the results it can be concluded that NaOCl and Ca(OCl)2, regardless of the concentration used, negatively affect the bond strength of adhesive materials to dentin.Este trabalho teve como objetivo avaliar a influência do Hipoclorito de Cálcio (Ca(OCl)2) sobre a resistência de união de materiais restauradores à dentina coronária. Para isso foram utilizados 90 incisivos centrais inferiores bovinos que foram cortados de modo a expor a dentina da câmara pulpar. Os espécimes foram divididos aleatoriamente em 9 grupos, de acordo com a solução utilizada. O Ca(OCl)2 foi utilizado como irrigante nas concentrações de 0,5%, 2,5% e 6%, com ou sem EDTA. O Hipoclorito de Sódio (NaOCl) também foi utilizado na concentração de 6%. Um grupo somente com EDTA e um grupo controle que não recebeu nenhum tratamento. Após ficar em contato com as substâncias dos respectivos grupos, a dentina foi condicionada com Ácido Fosfórico 37% e adesivo Ambar foi utilizado para hibridização dentinária. A restauração foi realizada com resina composta. Cada espécime foi cortada em cortadeira metalográfica, e assim obtendo os “palitos” que passaram por um teste de microtração. Para análise estatística foi utilizado o teste ANOVA seguido pelo teste de Tukey. Os resultados mostram que o grupo controle e aquele irrigado apenas com EDTA foram similares (P>0,05); os demais grupos foram similares entre si (P>0,05) e estatisticamente inferiores ao grupo controle (P>0,05). A partir dos resultados pode-se concluir que o NaOCl e o Ca(OCl)2, independente da concentração utilizada, afetam negativamente a resistência de união de materiais adesivos à dentina.Universidade de Passo FundoFaculdade de Odontologia - FOBrasilUPFCecchin, DoglasSala, Letícia2025-05-10T22:22:25Z2019-10-30info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/bachelorThesisapplication/pdfSALA, Letícia. Influência do hipoclorito de cálcio na resistência de união de materiais restauradores à dentina coronária. 2019. 27 f. Trabalho de Conclusão de Curso (Cirurgião-dentista). Curso de Odontologia. Universidade de Passo Fundo, Passo Fundo, 2019.https://repositorio.upf.br/handle/123456789/7363porinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UPFinstname:Universidade de Passo Fundo (UPF)instacron:UPF2025-12-30T19:52:17Zoai:repositorio.upf.br:123456789/7363Repositório InstitucionalPRIhttp://repositorio.upf.br/oai/requestjucelei@upf.br||biblio@upf.bropendoar:16102025-12-30T19:52:17Repositório Institucional da UPF - Universidade de Passo Fundo (UPF) |
| spellingShingle | Influência do hipoclorito de cálcio na resistência de união de materiais restauradores à dentina coronária Sala, Letícia Odontologia Dentina Hipoclorito de sódio Hipoclorito de cálcio |
| status_str | publishedVersion |
| title | Influência do hipoclorito de cálcio na resistência de união de materiais restauradores à dentina coronária |
| title_full | Influência do hipoclorito de cálcio na resistência de união de materiais restauradores à dentina coronária |
| title_fullStr | Influência do hipoclorito de cálcio na resistência de união de materiais restauradores à dentina coronária |
| title_full_unstemmed | Influência do hipoclorito de cálcio na resistência de união de materiais restauradores à dentina coronária |
| title_short | Influência do hipoclorito de cálcio na resistência de união de materiais restauradores à dentina coronária |
| title_sort | Influência do hipoclorito de cálcio na resistência de união de materiais restauradores à dentina coronária |
| topic | Odontologia Dentina Hipoclorito de sódio Hipoclorito de cálcio |
| url | https://repositorio.upf.br/handle/123456789/7363 |