Avaliação da resistência ao desgaste microabrasivo da liga Ti-12Cr revestida por filmes finos de TiN e CrN
Saved in:
| Main Author: | |
|---|---|
| Publication Date: | 2015 |
| Format: | Master thesis |
| Language: | por |
| Source: | Repositório Institucional da UnB |
| DOI: | http://dx.doi.org/10.26512/2015.06.D.18434 |
| Download full: | http://repositorio.unb.br/handle/10482/18434 http://dx.doi.org/10.26512/2015.06.D.18434 |
Summary: | Dissertação (mestrado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2015. |
| _version_ | 1871442556056764416 |
|---|---|
| author | Anicézio, Taise Maria Frazão de |
| author_browse | Anicézio, Taise Maria Frazão de |
| author_facet | Anicézio, Taise Maria Frazão de |
| author_role | author |
| bitstream.checksum.fl_str_mv | 4866e33daf9f1f9ccf75030b48561cce ccd909dbc82880f1b6d525677fb1df4d |
| bitstream.checksumAlgorithm.fl_str_mv | MD5 MD5 |
| bitstream.url.fl_str_mv | http://repositorio2.unb.br/jspui/bitstream/10482/18434/1/2015_TaiseMariaFrazaoDeAnicezio.pdf http://repositorio2.unb.br/jspui/bitstream/10482/18434/2/license.txt |
| collection | Repositório Institucional da UnB |
| contributor_str_mv | Silva, Cosme Roberto Moreira da |
| dc.contributor.advisor1.fl_str_mv | Silva, Cosme Roberto Moreira da |
| dc.contributor.author.fl_str_mv | Anicézio, Taise Maria Frazão de |
| dc.date.accessioned.fl_str_mv | 2015-07-14T11:18:33Z |
| dc.date.available.fl_str_mv | 2015-07-14T11:18:33Z |
| dc.date.issued.fl_str_mv | 2015-07-14 |
| dc.date.submitted.none.fl_str_mv | 2015-06-03 |
| dc.identifier.citation.fl_str_mv | ANICÉZIO, Taise Maria Frazão de. Avaliação da resistência ao desgaste microabrasivo da liga Ti-12Cr revestida por filmes finos de TiN e CrN. xv, 81 f., il. Dissertação (Mestrado em Ciências Mecânicas)—Universidade de Brasília, Brasília, 2015. |
| dc.identifier.doi.none.fl_str_mv | http://dx.doi.org/10.26512/2015.06.D.18434 |
| dc.identifier.uri.fl_str_mv | http://repositorio.unb.br/handle/10482/18434 |
| dc.language.iso.fl_str_mv | por |
| dc.rights.driver.fl_str_mv | info:eu-repo/semantics/openAccess |
| dc.source.none.fl_str_mv | reponame:Repositório Institucional da UnB instname:Universidade de Brasília (UnB) instacron:UNB |
| dc.subject.keyword.en.fl_str_mv | Ligas de titânio Resistência de materiais Desgaste microabrasivo Ligas (Metalurgia) |
| dc.title.alternative.en.fl_str_mv | Microabrasive wear resistance evaluation of alloy Ti-12Cr coated with thin films TiN AND CrN |
| dc.title.en.fl_str_mv | Avaliação da resistência ao desgaste microabrasivo da liga Ti-12Cr revestida por filmes finos de TiN e CrN |
| dc.type.driver.fl_str_mv | info:eu-repo/semantics/masterThesis |
| dc.type.status.fl_str_mv | info:eu-repo/semantics/publishedVersion |
| description | Dissertação (mestrado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2015. |
| eu_rights_str_mv | openAccess |
| format | masterThesis |
| id | UNB_dcc7bc892f4e9bd654420b2cc8534c72 |
| identifier_str_mv | ANICÉZIO, Taise Maria Frazão de. Avaliação da resistência ao desgaste microabrasivo da liga Ti-12Cr revestida por filmes finos de TiN e CrN. xv, 81 f., il. Dissertação (Mestrado em Ciências Mecânicas)—Universidade de Brasília, Brasília, 2015. |
| instacron_str | UNB |
| institution | UNB |
| instname_str | Universidade de Brasília (UnB) |
| language | por |
| network_acronym_str | UNB |
| network_name_str | Repositório Institucional da UnB |
| oai_identifier_str | oai:repositorio.unb.br:10482/18434 |
| publishDate | 2015 |
| publishDateSort | 2015 |
| reponame_str | Repositório Institucional da UnB |
| repository.mail.fl_str_mv | repositorio@unb.br |
| repository.name.fl_str_mv | Repositório Institucional da UnB - Universidade de Brasília (UnB) |
| repository_id_str | |
| spelling | Anicézio, Taise Maria Frazão deSilva, Cosme Roberto Moreira da2015-07-14T11:18:33Z2015-07-14T11:18:33Z2015-07-142015-06-03ANICÉZIO, Taise Maria Frazão de. Avaliação da resistência ao desgaste microabrasivo da liga Ti-12Cr revestida por filmes finos de TiN e CrN. xv, 81 f., il. Dissertação (Mestrado em Ciências Mecânicas)—Universidade de Brasília, Brasília, 2015.http://repositorio.unb.br/handle/10482/18434http://dx.doi.org/10.26512/2015.06.D.18434Dissertação (mestrado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2015.Titânio e suas ligas têm sido cada vez mais usados nos últimos anos em segmentos industriais bastante distintos como aeroespacial e biomateriais. Essa versatilidade devese ao fato de ser um material com elevada resistência mecânica, baixa densidade, alta resistência à corrosão e ótima biocompatibilidade. Todavia, não possuem boa resistência ao desgaste. Amostras da liga Ti-12Cr, produzidas por metalurgia do pó, foram revestidas por meio do processo PVD com filmes de Ti+TiN, Cr+CrN e Cr+CrN+TiN com o intuito de melhorar a resistência ao desgaste microabrasivo dessa liga. Um tribômetro do tipo esfera rotativa livre foi utilizado para gerar crateras de desgaste na superfície dos materiais estudados. Os diâmetros dessas calotas foram medidos e através do Método de Allsopp os coeficientes de desgaste abrasivo dos filmes e dos substratos foram então determinados. O filme Ti+TiN apresentou a melhor resistência ao desgaste dentre as amostras analisadas. A resistência ao desgaste seguiu a tendência das medidas de microdureza dos filmes, ou seja, o filme com maior microdureza, Ti+TiN, apresentou a melhor resistência ao desgaste, e também melhor adesão ao substrato. Os filmes Cr+CrN e Cr+CrN+TiN apresentaram coeficientes de desgaste do substrato e do filme com a mesma ordem de grandeza e valores que ficaram muito próximos porém, com microdurezas diferentes. Ambos os filmes apresentaram falha de adesão, de maneira que durante os ensaios de desgaste microabrasivo as partículas delaminadas dos filmes passaram a atuar juntamente com a suspensão abrasiva promovendo o aumento dos coeficientes de desgaste dessas amostras.Titanium and its alloys have been increasingly used in recent years in very different industrial segments such aerospace and biomaterials. This versatility is due to the fact that it is a material with high mechanical strength, low density, high corrosion resistance and good biocompatibility. However, have not good wear resistance. Samples of Ti-12Cr alloy produced by powder metallurgy were coated by PVD process with Ti+TiN, Cr+CrN and Cr+CrN+TiN films with the aim of microabrasive wear resistance improvement. A tribometer free rotating sphere type was used to generate wear craters on the surface of the materials studied. The diameters of these caps were measured and through Allsopp method the abrasive wear coefficient of the films and substrates were then determined. Ti+TiN film showed the best wear resistance among the analyzed samples. The wear resistance measurements followed the trend of micro-hardness of the films, i.e., the film with higher hardness, Ti+TiN, showed the best wear resistance, and also better adhesion to the substrate. The Cr+CrN and Cr+CrN+TiN exhibited wear coefficient of the substrate and the film of the same magnitude and values that were close but with different hardness. Both films showed adhesion failure, so that during the wear tests microabrasive particles of delaminated film began working together with the abrasive suspension promoting increased wear coefficient of the samples.Faculdade de Tecnologia (FT)Departamento de Engenharia Mecânica (FT ENM)Programa de Pós-Graduação em Ciências MecânicasA concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data.info:eu-repo/semantics/openAccessAvaliação da resistência ao desgaste microabrasivo da liga Ti-12Cr revestida por filmes finos de TiN e CrNMicroabrasive wear resistance evaluation of alloy Ti-12Cr coated with thin films TiN AND CrNinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisLigas de titânioResistência de materiaisDesgaste microabrasivoLigas (Metalurgia)porreponame:Repositório Institucional da UnBinstname:Universidade de Brasília (UnB)instacron:UNBORIGINAL2015_TaiseMariaFrazaoDeAnicezio.pdf2015_TaiseMariaFrazaoDeAnicezio.pdfapplication/pdf5322332http://repositorio2.unb.br/jspui/bitstream/10482/18434/1/2015_TaiseMariaFrazaoDeAnicezio.pdf4866e33daf9f1f9ccf75030b48561cceMD51open accessLICENSElicense.txtlicense.txttext/plain763http://repositorio2.unb.br/jspui/bitstream/10482/18434/2/license.txtccd909dbc82880f1b6d525677fb1df4dMD52open access10482/184342024-02-08 18:40:03.624open accessoai:repositorio.unb.br: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Repositório InstitucionalPUBhttps://repositorio.unb.br/oai/requestrepositorio@unb.bropendoar:2024-02-08T21:40:03Repositório Institucional da UnB - Universidade de Brasília (UnB) |
| spellingShingle | Avaliação da resistência ao desgaste microabrasivo da liga Ti-12Cr revestida por filmes finos de TiN e CrN Anicézio, Taise Maria Frazão de Ligas de titânio Resistência de materiais Desgaste microabrasivo Ligas (Metalurgia) |
| status_str | publishedVersion |
| title | Avaliação da resistência ao desgaste microabrasivo da liga Ti-12Cr revestida por filmes finos de TiN e CrN |
| title_full | Avaliação da resistência ao desgaste microabrasivo da liga Ti-12Cr revestida por filmes finos de TiN e CrN |
| title_fullStr | Avaliação da resistência ao desgaste microabrasivo da liga Ti-12Cr revestida por filmes finos de TiN e CrN |
| title_full_unstemmed | Avaliação da resistência ao desgaste microabrasivo da liga Ti-12Cr revestida por filmes finos de TiN e CrN |
| title_short | Avaliação da resistência ao desgaste microabrasivo da liga Ti-12Cr revestida por filmes finos de TiN e CrN |
| title_sort | Avaliação da resistência ao desgaste microabrasivo da liga Ti-12Cr revestida por filmes finos de TiN e CrN |
| topic | Ligas de titânio Resistência de materiais Desgaste microabrasivo Ligas (Metalurgia) |
| url | http://repositorio.unb.br/handle/10482/18434 http://dx.doi.org/10.26512/2015.06.D.18434 |