Estudos da sinterização de Bi12TiO20 (BTO) visando obter cerâmicas transparentes
Guardat en:
| Autor principal: | |
|---|---|
| Data de publicació: | 2011 |
| Format: | Master thesis |
| Idioma: | por |
| Font: | Repositório Institucional da UFG |
| Download full: | http://repositorio.bc.ufg.br/tede/handle/tde/804 |
Sumari: | This work presents the systematic results of studies concerning the sintering of the Bi12TiO20 (BTO) aiming the production of transparent ceramic samples. All that because the BTO is a material that has great scientific and technologic visibility due to its optical, electro and electro-optical properties, but still little explored as ceramic. The sintering starting material was obtained by solid state reaction between Bi2O3 e TiO2; the synthesized BTO was grinded in ball milling until sub micrometric sizes. The conditions for preparing green samples were also investigated, allowing samples with green relative density between 58% and 62%, with uniaxial and isostatic pressing techniques. The study of the sintering process involved different sintering programs, under different atmospheres conditions and additive utilization. Optimized conditions were established and the limiting factors discussed. The quality of the obtained ceramics was assessed by their final relative density, phase homogeneity, microstructure and optical properties (transmission, optical activity and electro-optical performance). Samples with relative density above 99,9% and 50% of the monocrystal´s optical transmission in the 633 nm wavelength and equal optical activity were obtained. Nevertheless, the ceramics still show scattering centers and none liquid electro-optical effect was observed. |
| _version_ | 1871426418637799424 |
|---|---|
| author | AMARAL, Thiago Martins |
| author_browse | AMARAL, Thiago Martins |
| author_facet | AMARAL, Thiago Martins |
| author_role | author |
| bitstream.checksum.fl_str_mv | ece5cabfa428decf86242ad3624c5852 a01ea307af87b83e2cbc3003f0b88dd9 6f3e8c8937745e405f4fc132d43f841d |
| bitstream.checksumAlgorithm.fl_str_mv | MD5 MD5 MD5 |
| bitstream.url.fl_str_mv | http://repositorio.bc.ufg.br/tede/bitstreams/43c887dd-a985-46fe-ae1f-c342f3007dc4/download http://repositorio.bc.ufg.br/tede/bitstreams/4c82902a-25b2-4d91-acb6-ee45b10cd8c5/download http://repositorio.bc.ufg.br/tede/bitstreams/f1a1208d-6662-47e1-95ec-5f685142c39e/download |
| collection | Repositório Institucional da UFG |
| contributor_str_mv | CARVALHO, Jesiel Freitas |
| dc.contributor.advisor1.fl_str_mv | CARVALHO, Jesiel Freitas |
| dc.contributor.advisor1Lattes.fl_str_mv | http://lattes.cnpq.br/5841291496427516 |
| dc.contributor.author.fl_str_mv | AMARAL, Thiago Martins |
| dc.contributor.authorLattes.fl_str_mv | http://lattes.cnpq.br/4337492660554921 |
| dc.date.accessioned.fl_str_mv | 2014-07-29T15:07:08Z |
| dc.date.available.fl_str_mv | 2011-04-14 |
| dc.date.issued.fl_str_mv | 2011-02-16 |
| dc.format.none.fl_str_mv | application/pdf |
| dc.identifier.citation.fl_str_mv | AMARAL, Thiago Martins. Studies of sintering Bi12TiO20 (BTO) in order obtain transparent ceramics. 2011. 83 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de Goiás, Goiânia, 2011. |
| dc.identifier.uri.fl_str_mv | http://repositorio.bc.ufg.br/tede/handle/tde/804 |
| dc.language.iso.fl_str_mv | por |
| dc.publisher.country.fl_str_mv | BR |
| dc.publisher.department.fl_str_mv | Ciências Exatas e da Terra |
| dc.publisher.initials.fl_str_mv | UFG |
| dc.publisher.none.fl_str_mv | Universidade Federal de Goiás |
| dc.publisher.program.fl_str_mv | Mestrado em Física |
| dc.rights.driver.fl_str_mv | info:eu-repo/semantics/openAccess |
| dc.source.none.fl_str_mv | reponame:Repositório Institucional da UFG instname:Universidade Federal de Goiás (UFG) instacron:UFG |
| dc.subject.cnpq.fl_str_mv | CNPQ::CIENCIAS EXATAS E DA TERRA::FISICA |
| dc.subject.eng.fl_str_mv | Bismuth titanate sintering ceramics transparent |
| dc.subject.por.fl_str_mv | Titanato de bismuto sinterização cerâmica transparente 1.Titanato de bismuto - Sinterização 2.Cerâmica transparente |
| dc.title.alternative.eng.fl_str_mv | Studies of sintering Bi12TiO20 (BTO) in order obtain transparent ceramics |
| dc.title.por.fl_str_mv | Estudos da sinterização de Bi12TiO20 (BTO) visando obter cerâmicas transparentes |
| dc.type.driver.fl_str_mv | info:eu-repo/semantics/masterThesis |
| dc.type.status.fl_str_mv | info:eu-repo/semantics/publishedVersion |
| description | This work presents the systematic results of studies concerning the sintering of the Bi12TiO20 (BTO) aiming the production of transparent ceramic samples. All that because the BTO is a material that has great scientific and technologic visibility due to its optical, electro and electro-optical properties, but still little explored as ceramic. The sintering starting material was obtained by solid state reaction between Bi2O3 e TiO2; the synthesized BTO was grinded in ball milling until sub micrometric sizes. The conditions for preparing green samples were also investigated, allowing samples with green relative density between 58% and 62%, with uniaxial and isostatic pressing techniques. The study of the sintering process involved different sintering programs, under different atmospheres conditions and additive utilization. Optimized conditions were established and the limiting factors discussed. The quality of the obtained ceramics was assessed by their final relative density, phase homogeneity, microstructure and optical properties (transmission, optical activity and electro-optical performance). Samples with relative density above 99,9% and 50% of the monocrystal´s optical transmission in the 633 nm wavelength and equal optical activity were obtained. Nevertheless, the ceramics still show scattering centers and none liquid electro-optical effect was observed. |
| eu_rights_str_mv | openAccess |
| format | masterThesis |
| id | UFG-2_d4cb4f350ca411ee8e2beec2b7af4cc3 |
| identifier_str_mv | AMARAL, Thiago Martins. Studies of sintering Bi12TiO20 (BTO) in order obtain transparent ceramics. 2011. 83 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de Goiás, Goiânia, 2011. |
| instacron_str | UFG |
| institution | UFG |
| instname_str | Universidade Federal de Goiás (UFG) |
| language | por |
| network_acronym_str | UFG-2 |
| network_name_str | Repositório Institucional da UFG |
| oai_identifier_str | oai:repositorio.bc.ufg.br:tde/804 |
| publishDate | 2011 |
| publishDateSort | 2011 |
| publisher.none.fl_str_mv | Universidade Federal de Goiás |
| reponame_str | Repositório Institucional da UFG |
| repository.mail.fl_str_mv | grt.bc@ufg.br |
| repository.name.fl_str_mv | Repositório Institucional da UFG - Universidade Federal de Goiás (UFG) |
| repository_id_str | oai:repositorio.bc.ufg.br:tede/1234 |
| spelling | CARVALHO, Jesiel Freitashttp://lattes.cnpq.br/5841291496427516http://lattes.cnpq.br/4337492660554921AMARAL, Thiago Martins2014-07-29T15:07:08Z2011-04-142011-02-16AMARAL, Thiago Martins. Studies of sintering Bi12TiO20 (BTO) in order obtain transparent ceramics. 2011. 83 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de Goiás, Goiânia, 2011.http://repositorio.bc.ufg.br/tede/handle/tde/804This work presents the systematic results of studies concerning the sintering of the Bi12TiO20 (BTO) aiming the production of transparent ceramic samples. All that because the BTO is a material that has great scientific and technologic visibility due to its optical, electro and electro-optical properties, but still little explored as ceramic. The sintering starting material was obtained by solid state reaction between Bi2O3 e TiO2; the synthesized BTO was grinded in ball milling until sub micrometric sizes. The conditions for preparing green samples were also investigated, allowing samples with green relative density between 58% and 62%, with uniaxial and isostatic pressing techniques. The study of the sintering process involved different sintering programs, under different atmospheres conditions and additive utilization. Optimized conditions were established and the limiting factors discussed. The quality of the obtained ceramics was assessed by their final relative density, phase homogeneity, microstructure and optical properties (transmission, optical activity and electro-optical performance). Samples with relative density above 99,9% and 50% of the monocrystal´s optical transmission in the 633 nm wavelength and equal optical activity were obtained. Nevertheless, the ceramics still show scattering centers and none liquid electro-optical effect was observed.Neste trabalho são apresentados resultados de estudos sistemáticos referentes à sinterização do Bi12TiO20 (BTO) visando a obtenção de amostras cerâmicas transparentes. Isso porque o BTO é um material de grande interesse científico e tecnológico devido às suas propriedades ópticas, elétricas e eletroópticas, mas ainda pouco explorado como cerâmica. O material de partida para sinterização foi obtido por reação no estado sólido entre Bi2O3 e TiO2; o BTO assim sintetizado foi moído em moinho de bolas até tamanhos submicrométricos. As condições de preparação de pastilhas a verde foram investigadas, permitindo a obtenção de corpos com densidade relativa a verde, entre 58% e 62%, com uso de prensagem uniaxial e isostática. O estudo do processo de sinterização envolveu avaliar diferentes rampas de aquecimento, atmosfera de sinterização e utilização de aditivos. Condições otimizadas foram estabelecidas e os fatores limitantes discutidos. As cerâmicas foram avaliadas com respeito à densidade relativa final, homogeneidade de fase, microestrutura e propriedades ópticas (transmissividade, atividade óptica e modulação eletro-óptica). Amostras com densidade relativa maior que 99,9%, transmitância óptica de até 50% daquela do monocristal em 633 nm e atividade óptica idêntica foram obtidas. No entanto, as cerâmicas ainda apresentam centros espalhadores e nenhum efeito líquido de modulação eletro-óptica foi observado.application/pdfhttp://repositorio.bc.ufg.br/TEDE/retrieve/3592/Mestrado_Thiago_Martins_Amaral.pdf.jpgporUniversidade Federal de GoiásMestrado em FísicaUFGBRCiências Exatas e da TerraTitanato de bismutosinterizaçãocerâmica transparente1.Titanato de bismuto - Sinterização 2.Cerâmica transparenteBismuth titanatesintering ceramics transparentCNPQ::CIENCIAS EXATAS E DA TERRA::FISICAEstudos da sinterização de Bi12TiO20 (BTO) visando obter cerâmicas transparentesStudies of sintering Bi12TiO20 (BTO) in order obtain transparent ceramicsinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFGinstname:Universidade Federal de Goiás (UFG)instacron:UFGORIGINALMestrado_Thiago_Martins_Amaral.pdfapplication/pdf3609467http://repositorio.bc.ufg.br/tede/bitstreams/43c887dd-a985-46fe-ae1f-c342f3007dc4/downloadece5cabfa428decf86242ad3624c5852MD51TEXTMestrado_Thiago_Martins_Amaral.pdf.txtMestrado_Thiago_Martins_Amaral.pdf.txtExtracted Texttext/plain101585http://repositorio.bc.ufg.br/tede/bitstreams/4c82902a-25b2-4d91-acb6-ee45b10cd8c5/downloada01ea307af87b83e2cbc3003f0b88dd9MD52THUMBNAILMestrado_Thiago_Martins_Amaral.pdf.jpgMestrado_Thiago_Martins_Amaral.pdf.jpgGenerated Thumbnailimage/jpeg4438http://repositorio.bc.ufg.br/tede/bitstreams/f1a1208d-6662-47e1-95ec-5f685142c39e/download6f3e8c8937745e405f4fc132d43f841dMD53tde/8042014-07-30 03:06:45.929open.accessoai:repositorio.bc.ufg.br:tde/804http://repositorio.bc.ufg.br/tedeRepositório InstitucionalPUBhttps://repositorio.bc.ufg.br/tedeserver/oai/requestgrt.bc@ufg.bropendoar:oai:repositorio.bc.ufg.br:tede/12342014-07-30T06:06:45Repositório Institucional da UFG - Universidade Federal de Goiás (UFG) |
| spellingShingle | Estudos da sinterização de Bi12TiO20 (BTO) visando obter cerâmicas transparentes AMARAL, Thiago Martins Titanato de bismuto sinterização cerâmica transparente 1.Titanato de bismuto - Sinterização 2.Cerâmica transparente Bismuth titanate sintering ceramics transparent CNPQ::CIENCIAS EXATAS E DA TERRA::FISICA |
| status_str | publishedVersion |
| title | Estudos da sinterização de Bi12TiO20 (BTO) visando obter cerâmicas transparentes |
| title_full | Estudos da sinterização de Bi12TiO20 (BTO) visando obter cerâmicas transparentes |
| title_fullStr | Estudos da sinterização de Bi12TiO20 (BTO) visando obter cerâmicas transparentes |
| title_full_unstemmed | Estudos da sinterização de Bi12TiO20 (BTO) visando obter cerâmicas transparentes |
| title_short | Estudos da sinterização de Bi12TiO20 (BTO) visando obter cerâmicas transparentes |
| title_sort | Estudos da sinterização de Bi12TiO20 (BTO) visando obter cerâmicas transparentes |
| topic | Titanato de bismuto sinterização cerâmica transparente 1.Titanato de bismuto - Sinterização 2.Cerâmica transparente Bismuth titanate sintering ceramics transparent CNPQ::CIENCIAS EXATAS E DA TERRA::FISICA |
| url | http://repositorio.bc.ufg.br/tede/handle/tde/804 |