Influência de tratamentos superficiais na resistência de união de reparo em resina a base de silorano: análise após envelhecimento
محفوظ في:
| المؤلف الرئيسي: | |
|---|---|
| تاريخ النشر: | 2011 |
| التنسيق: | Master thesis |
| اللغة: | por |
| المصدر: | Repositório Institucional da UFG |
| Download full: | http://repositorio.bc.ufg.br/tede/handle/tede/3762 |
الملخص: | The aim of the present study was to evaluate the influence of different surface treatments on bond strength of repair resin-based silorane through microtensile test. 160 silorane blocks were randomly distributed among 40 experimental groups (n=4) resulting from the interaction of three factors under study: surface treatment, adhesive system and resin used to repair. The blocks were stored for 9 days in deionized water at 37°C prior to surface treatment and repair. Repair was performed, after the use of a bonding agent: (Ad 1) Silorane bond or (Ad 2) Adper Scotchbond, with Filtek P90 (P90) or Filtek Z350 XT (Z350 XT) on one of the 10 treatment protocols: control (C), silane (Si), phosphoric acid (Pa), Pa plus Si (PaSi), hydrofluoric acid (Ha), Ha plus Si (HaSi), sandblasting (S), S plus Si (SSi), diamond bur (Db), Db plus Si (DbSi). Blocks were sectioned into beams and after age by storage for six months, subjected to microtensile testing and subsequent analysis in a stereoscope to define the failure types. Additionally, 10 blocks of Filtek P90 composite resin were made for surface analysis by SEM, after completion of surface treatment. Statistical analysis (Mann-Whitney, Kruskal- Wallis and Dunn tests, α=0.05) was performed. The values were statistically influenced by the type of resin (p<0.001) and by the surface treatment (p<0.0001), but not by the bonding agent (p=0,940). SSi, Ha and HaSi produced similar bond strength values, the greatest. Treating the surface with Db showed the worst values and composite resin P90 generated higher bond strength values than Z350 XT to repair silorane surfaces. |
| _version_ | 1871426417864998912 |
|---|---|
| author | Guimarães, Raphaella Mendes |
| author_browse | Guimarães, Raphaella Mendes |
| author_facet | Guimarães, Raphaella Mendes |
| author_role | author |
| bitstream.checksum.fl_str_mv | bd3efa91386c1718a7f26a329fdcb468 4afdbb8c545fd630ea7db775da747b2f 1e0094e9d8adcf16b18effef4ce7ed83 9da0b6dfac957114c6a7714714b86306 05767b0e186652fc39182ebc611cd207 e4bb1e4ba92452a473c960f366782079 9f6d2bfd5c192a9fef62a5b34c873447 |
| bitstream.checksumAlgorithm.fl_str_mv | MD5 MD5 MD5 MD5 MD5 MD5 MD5 |
| bitstream.url.fl_str_mv | http://repositorio.bc.ufg.br/tede/bitstreams/03e603f3-319f-4c63-851c-607c8e1cffca/download http://repositorio.bc.ufg.br/tede/bitstreams/b0359103-b162-476d-8dd0-819ddc6dfd92/download http://repositorio.bc.ufg.br/tede/bitstreams/887fdceb-294e-45d7-b679-4452d4593dbb/download http://repositorio.bc.ufg.br/tede/bitstreams/317a4459-32a3-448e-ba51-b3d1e2c5bbbf/download http://repositorio.bc.ufg.br/tede/bitstreams/cf794d12-a618-446d-9771-4ca7a516acb9/download http://repositorio.bc.ufg.br/tede/bitstreams/e7a5fd6f-c971-45ed-8365-7e2ec6a08d18/download http://repositorio.bc.ufg.br/tede/bitstreams/54f6e9ab-b0b0-484a-9dda-1d5bed5e52b3/download |
| collection | Repositório Institucional da UFG |
| contributor_str_mv | Souza, João Batista de Lopes, Lawrence Gonzaga Souza, João Batista de Lopes, Lawrence Gonzaga Carlo, Hugo Lemes Cardoso, Paula de Carvalho |
| dc.contributor.advisor-co1.fl_str_mv | Lopes, Lawrence Gonzaga |
| dc.contributor.advisor1.fl_str_mv | Souza, João Batista de |
| dc.contributor.advisor1Lattes.fl_str_mv | http://lattes.cnpq.br/0642108682158061 |
| dc.contributor.author.fl_str_mv | Guimarães, Raphaella Mendes |
| dc.contributor.referee1.fl_str_mv | Souza, João Batista de |
| dc.contributor.referee2.fl_str_mv | Lopes, Lawrence Gonzaga |
| dc.contributor.referee3.fl_str_mv | Carlo, Hugo Lemes |
| dc.contributor.referee4.fl_str_mv | Cardoso, Paula de Carvalho |
| dc.date.accessioned.fl_str_mv | 2014-12-08T11:50:47Z |
| dc.date.issued.fl_str_mv | 2011-12-23 |
| dc.format.none.fl_str_mv | application/pdf |
| dc.identifier.citation.fl_str_mv | GUIMARÃES, Raphaella Mendes. Influência de tratamentos superficiais na resistência de união de reparo em resina a base de silorano: análise após envelhecimento. 2011. 70 f. Dissertação (Mestrado em Odontologia) - Universidade Federal de Goiás, Goiânia, 2011. |
| dc.identifier.uri.fl_str_mv | http://repositorio.bc.ufg.br/tede/handle/tede/3762 |
| dc.language.iso.fl_str_mv | por |
| dc.publisher.country.fl_str_mv | Brasil |
| dc.publisher.department.fl_str_mv | Faculdade de Odontologia - FO (RG) |
| dc.publisher.initials.fl_str_mv | UFG |
| dc.publisher.none.fl_str_mv | Universidade Federal de Goiás |
| dc.publisher.program.fl_str_mv | Programa de Pós-graduação em Odontologia (FO) |
| dc.relation.cnpq.fl_str_mv | -1816740449898491657 |
| dc.relation.confidence.fl_str_mv | 600 600 600 600 |
| dc.relation.department.fl_str_mv | -5569154581575113691 |
| dc.relation.program.fl_str_mv | -2325576619034292269 |
| dc.relation.sponsorship.fl_str_mv | 2075167498588264571 |
| dc.rights.driver.fl_str_mv | http://creativecommons.org/licenses/by-nc-nd/4.0/ info:eu-repo/semantics/openAccess |
| dc.source.none.fl_str_mv | reponame:Repositório Institucional da UFG instname:Universidade Federal de Goiás (UFG) instacron:UFG |
| dc.subject.cnpq.fl_str_mv | ODONTOLOGIA::CLINICA ODONTOLOGICA |
| dc.subject.eng.fl_str_mv | Dental restoration failure Dental materials Composite resins |
| dc.subject.por.fl_str_mv | Falha de restauração dentária Materiais dentários Resinas compostas |
| dc.title.alternative.eng.fl_str_mv | Influence of surface treatment on band strength of repair resin-based silorane: analysis after aging |
| dc.title.por.fl_str_mv | Influência de tratamentos superficiais na resistência de união de reparo em resina a base de silorano: análise após envelhecimento |
| dc.type.driver.fl_str_mv | info:eu-repo/semantics/masterThesis |
| dc.type.status.fl_str_mv | info:eu-repo/semantics/publishedVersion |
| description | The aim of the present study was to evaluate the influence of different surface treatments on bond strength of repair resin-based silorane through microtensile test. 160 silorane blocks were randomly distributed among 40 experimental groups (n=4) resulting from the interaction of three factors under study: surface treatment, adhesive system and resin used to repair. The blocks were stored for 9 days in deionized water at 37°C prior to surface treatment and repair. Repair was performed, after the use of a bonding agent: (Ad 1) Silorane bond or (Ad 2) Adper Scotchbond, with Filtek P90 (P90) or Filtek Z350 XT (Z350 XT) on one of the 10 treatment protocols: control (C), silane (Si), phosphoric acid (Pa), Pa plus Si (PaSi), hydrofluoric acid (Ha), Ha plus Si (HaSi), sandblasting (S), S plus Si (SSi), diamond bur (Db), Db plus Si (DbSi). Blocks were sectioned into beams and after age by storage for six months, subjected to microtensile testing and subsequent analysis in a stereoscope to define the failure types. Additionally, 10 blocks of Filtek P90 composite resin were made for surface analysis by SEM, after completion of surface treatment. Statistical analysis (Mann-Whitney, Kruskal- Wallis and Dunn tests, α=0.05) was performed. The values were statistically influenced by the type of resin (p<0.001) and by the surface treatment (p<0.0001), but not by the bonding agent (p=0,940). SSi, Ha and HaSi produced similar bond strength values, the greatest. Treating the surface with Db showed the worst values and composite resin P90 generated higher bond strength values than Z350 XT to repair silorane surfaces. |
| eu_rights_str_mv | openAccess |
| format | masterThesis |
| id | UFG-2_d3981fcaee5effd7632efec26b6fd34f |
| identifier_str_mv | GUIMARÃES, Raphaella Mendes. Influência de tratamentos superficiais na resistência de união de reparo em resina a base de silorano: análise após envelhecimento. 2011. 70 f. Dissertação (Mestrado em Odontologia) - Universidade Federal de Goiás, Goiânia, 2011. |
| instacron_str | UFG |
| institution | UFG |
| instname_str | Universidade Federal de Goiás (UFG) |
| language | por |
| network_acronym_str | UFG-2 |
| network_name_str | Repositório Institucional da UFG |
| oai_identifier_str | oai:repositorio.bc.ufg.br:tede/3762 |
| publishDate | 2011 |
| publishDateSort | 2011 |
| publisher.none.fl_str_mv | Universidade Federal de Goiás |
| reponame_str | Repositório Institucional da UFG |
| repository.mail.fl_str_mv | grt.bc@ufg.br |
| repository.name.fl_str_mv | Repositório Institucional da UFG - Universidade Federal de Goiás (UFG) |
| repository_id_str | oai:repositorio.bc.ufg.br:tede/1234 |
| rights_invalid_str_mv | http://creativecommons.org/licenses/by-nc-nd/4.0/ |
| spelling | Souza, João Batista dehttp://lattes.cnpq.br/0642108682158061Lopes, Lawrence GonzagaSouza, João Batista deLopes, Lawrence GonzagaCarlo, Hugo LemesCardoso, Paula de CarvalhoGuimarães, Raphaella Mendes2014-12-08T11:50:47Z2011-12-23GUIMARÃES, Raphaella Mendes. Influência de tratamentos superficiais na resistência de união de reparo em resina a base de silorano: análise após envelhecimento. 2011. 70 f. Dissertação (Mestrado em Odontologia) - Universidade Federal de Goiás, Goiânia, 2011.http://repositorio.bc.ufg.br/tede/handle/tede/3762The aim of the present study was to evaluate the influence of different surface treatments on bond strength of repair resin-based silorane through microtensile test. 160 silorane blocks were randomly distributed among 40 experimental groups (n=4) resulting from the interaction of three factors under study: surface treatment, adhesive system and resin used to repair. The blocks were stored for 9 days in deionized water at 37°C prior to surface treatment and repair. Repair was performed, after the use of a bonding agent: (Ad 1) Silorane bond or (Ad 2) Adper Scotchbond, with Filtek P90 (P90) or Filtek Z350 XT (Z350 XT) on one of the 10 treatment protocols: control (C), silane (Si), phosphoric acid (Pa), Pa plus Si (PaSi), hydrofluoric acid (Ha), Ha plus Si (HaSi), sandblasting (S), S plus Si (SSi), diamond bur (Db), Db plus Si (DbSi). Blocks were sectioned into beams and after age by storage for six months, subjected to microtensile testing and subsequent analysis in a stereoscope to define the failure types. Additionally, 10 blocks of Filtek P90 composite resin were made for surface analysis by SEM, after completion of surface treatment. Statistical analysis (Mann-Whitney, Kruskal- Wallis and Dunn tests, α=0.05) was performed. The values were statistically influenced by the type of resin (p<0.001) and by the surface treatment (p<0.0001), but not by the bonding agent (p=0,940). SSi, Ha and HaSi produced similar bond strength values, the greatest. Treating the surface with Db showed the worst values and composite resin P90 generated higher bond strength values than Z350 XT to repair silorane surfaces.O objetivo deste estudo foi avaliar a influência de diferentes tratamentos superficiais na resistência de união de reparo em resina composta à base de silorano, por meio de ensaio de microtração. Foram aleatoriamente distribuídos 160 blocos de resina composta a base de silorano em 40 grupos experimentais (n=4) resultantes da interação entre 3 fatores em estudo: tratamento superficial, sistema adesivo e resina para realizar o reparo. Os blocos confeccionados foram armazenados durante 9 dias em água deionizada a 37°C previamente à realização do tratamento superficial e reparo. O reparo foi realizado após a aplicação do sistema adesivo silorano da Filtek P90 (Ad 1) ou do sistema adesivo Adper Scotchbond Multi-uso (Ad 2), com a resina composta Filtek P90 (P90) ou Filtek Z350 XT (Z350 XT), em um dos dez diferentes tipos de tratamento superficial: controle (C), silano (Si), ácido fosfórico (Af), Af e Si (AfSi), ácido hidrofluorídrico (Ah), Ah e Si (AhSi), jateamento (J), J e Si (JSi), ranhuras (R), R e Si (RSi). Os blocos foram seccionados em forma de palito, em seguida armazenados por seis meses, e então submetidos ao ensaio de microtração e posterior análise em lupa estereoscópica para definição do padrão de fratura. Adicionalmente, foram confeccionados 10 blocos de resina composta Filtek P90 para análise da superfície em MEV, após a realização dos tratamentos superficiais. Os dados obtidos foram submetidos a análise estatística (Mann-Whitney, Kruskal-Wallis e Dunn, α=0,05). Pôde-se verificar que os valores de resistência de união foram estatisticamente influenciados pelo tipo de resina (p<0.001) e pelos tratamentos superficiais (p<0.0001), porém não houve diferença para os adesivos (p= 0,940). JSi, Ah e AhSi foram semelhantes entre si e apresentaram os maiores valores. O emprego de ranhuras resultou nos piores resultados e a resina P90 proporcionou maiores valores de resistência de união do que a resina Z350 XT para reparo em resina composta a base de silorano.Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://repositorio.bc.ufg.br/tede/retrieve/13446/Disserta%c3%a7%c3%a3o%20-%20Raphaella%20Mendes%20Guimar%c3%a3es%20-%202011.pdf.jpgporUniversidade Federal de GoiásPrograma de Pós-graduação em Odontologia (FO)UFGBrasilFaculdade de Odontologia - FO (RG)http://creativecommons.org/licenses/by-nc-nd/4.0/info:eu-repo/semantics/openAccessFalha de restauração dentáriaMateriais dentáriosResinas compostasDental restoration failureDental materialsComposite resinsODONTOLOGIA::CLINICA ODONTOLOGICAInfluência de tratamentos superficiais na resistência de união de reparo em resina a base de silorano: análise após envelhecimentoInfluence of surface treatment on band strength of repair resin-based silorane: analysis after aginginfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-2325576619034292269600600600600-5569154581575113691-18167404498984916572075167498588264571reponame:Repositório Institucional da UFGinstname:Universidade Federal de Goiás (UFG)instacron:UFGLICENSElicense.txtlicense.txttext/plain; charset=utf-82165http://repositorio.bc.ufg.br/tede/bitstreams/03e603f3-319f-4c63-851c-607c8e1cffca/downloadbd3efa91386c1718a7f26a329fdcb468MD51CC-LICENSElicense_urllicense_urltext/plain; charset=utf-849http://repositorio.bc.ufg.br/tede/bitstreams/b0359103-b162-476d-8dd0-819ddc6dfd92/download4afdbb8c545fd630ea7db775da747b2fMD52license_textlicense_texttext/html; charset=utf-822302http://repositorio.bc.ufg.br/tede/bitstreams/887fdceb-294e-45d7-b679-4452d4593dbb/download1e0094e9d8adcf16b18effef4ce7ed83MD53license_rdflicense_rdfapplication/rdf+xml; charset=utf-823148http://repositorio.bc.ufg.br/tede/bitstreams/317a4459-32a3-448e-ba51-b3d1e2c5bbbf/download9da0b6dfac957114c6a7714714b86306MD54ORIGINALDissertação - Raphaella Mendes Guimarães - 2011.pdfDissertação - Raphaella Mendes Guimarães - 2011.pdfapplication/pdf11646606http://repositorio.bc.ufg.br/tede/bitstreams/cf794d12-a618-446d-9771-4ca7a516acb9/download05767b0e186652fc39182ebc611cd207MD55TEXTDissertação - Raphaella Mendes Guimarães - 2011.pdf.txtDissertação - Raphaella Mendes Guimarães - 2011.pdf.txtExtracted Texttext/plain86778http://repositorio.bc.ufg.br/tede/bitstreams/e7a5fd6f-c971-45ed-8365-7e2ec6a08d18/downloade4bb1e4ba92452a473c960f366782079MD56THUMBNAILDissertação - Raphaella Mendes Guimarães - 2011.pdf.jpgDissertação - Raphaella Mendes Guimarães - 2011.pdf.jpgGenerated Thumbnailimage/jpeg2916http://repositorio.bc.ufg.br/tede/bitstreams/54f6e9ab-b0b0-484a-9dda-1d5bed5e52b3/download9f6d2bfd5c192a9fef62a5b34c873447MD57tede/37622014-12-09 03:01:17.244http://creativecommons.org/licenses/by-nc-nd/4.0/Acesso Abertoopen.accessoai:repositorio.bc.ufg.br:tede/3762http://repositorio.bc.ufg.br/tedeRepositório InstitucionalPUBhttps://repositorio.bc.ufg.br/tedeserver/oai/requestgrt.bc@ufg.bropendoar:oai:repositorio.bc.ufg.br:tede/12342014-12-09T05:01:17Repositório Institucional da UFG - Universidade Federal de Goiás (UFG)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 |
| spellingShingle | Influência de tratamentos superficiais na resistência de união de reparo em resina a base de silorano: análise após envelhecimento Guimarães, Raphaella Mendes Falha de restauração dentária Materiais dentários Resinas compostas Dental restoration failure Dental materials Composite resins ODONTOLOGIA::CLINICA ODONTOLOGICA |
| status_str | publishedVersion |
| title | Influência de tratamentos superficiais na resistência de união de reparo em resina a base de silorano: análise após envelhecimento |
| title_full | Influência de tratamentos superficiais na resistência de união de reparo em resina a base de silorano: análise após envelhecimento |
| title_fullStr | Influência de tratamentos superficiais na resistência de união de reparo em resina a base de silorano: análise após envelhecimento |
| title_full_unstemmed | Influência de tratamentos superficiais na resistência de união de reparo em resina a base de silorano: análise após envelhecimento |
| title_short | Influência de tratamentos superficiais na resistência de união de reparo em resina a base de silorano: análise após envelhecimento |
| title_sort | Influência de tratamentos superficiais na resistência de união de reparo em resina a base de silorano: análise após envelhecimento |
| topic | Falha de restauração dentária Materiais dentários Resinas compostas Dental restoration failure Dental materials Composite resins ODONTOLOGIA::CLINICA ODONTOLOGICA |
| url | http://repositorio.bc.ufg.br/tede/handle/tede/3762 |