Estudo da aderência no reparo com concreto autoadensável (CAA): influência do preparo da superfície, da resistência à compressão do concreto da base e do tipo do concreto (convencional e CAA)
Gespeichert in:
| 1. Verfasser: | |
|---|---|
| Publikationsdatum: | 2011 |
| Format: | Master thesis |
| Sprache: | por |
| Quelle: | Repositório Institucional da UFG |
| Download full: | http://repositorio.bc.ufg.br/tede/handle/tede/4190 |
Zusammenfassung: | Efficient repairs in concrete structures require perfect bonding between the base concrete and the applied concrete. The experimental analysis shown in this study focused on how bonding is influenced by three types of base concrete preparation: hydro-jet blasting (BHD), manual scabbling (BMA) and mechanical scabbling (BME), as well as two types of base surface condition: dry (0%) and humid (100%) and also by the application of three different types of bonding agents: B - cement + water; C – cement + water + additive superplasticizer; D – cement + water + additive superplasticizer + active sílica. Fifteen conventional concrete bases prepared using concrete with compressive strength of class C20 and fifteen self-consolidating concrete bases with compressive strength of class C30 were tested. Surface roughness was characterized using profiles according to parameters Ra (standard deviation with respect to an average line) and Rz (average height between consecutives peaks and valleys). Self-consolidating concrete with C40 compressive strength was used to repair the concrete bases. Dyna Proceq apparatus was used to determine tension bonding strength. The hydro-jet blasting (BHD) preparation presented the lowest surface roughness values and the highest bonding strength results as well as the lowest values of the coefficient of variation. The manual scabbling (BMA) preparation presented intermediary results. The mechanical scabbling (BME) preparation presented the highest surface roughness values and the lowest bonding strength results. Surface humidity increase the number of concrete base ruptures. The use of bonding agents increased bonding strength regardless of the degree of surface humidity. |
| _version_ | 1871426402922790912 |
|---|---|
| author | Rocha, Adilson Pereira da |
| author_browse | Rocha, Adilson Pereira da |
| author_facet | Rocha, Adilson Pereira da |
| author_role | author |
| bitstream.checksum.fl_str_mv | bd3efa91386c1718a7f26a329fdcb468 4afdbb8c545fd630ea7db775da747b2f b292a83e42bd8ad62533bba1395b83ff 9da0b6dfac957114c6a7714714b86306 6084758e786d92b3d0b54e276271b54f ff640dc4766163a366eb69d0dd2517b2 5c1b699b8d954fb5aee53f4de7f829ff |
| bitstream.checksumAlgorithm.fl_str_mv | MD5 MD5 MD5 MD5 MD5 MD5 MD5 |
| bitstream.url.fl_str_mv | http://repositorio.bc.ufg.br/tede/bitstreams/bf2e0baa-2629-47e4-a61a-51d9d98482ba/download http://repositorio.bc.ufg.br/tede/bitstreams/b25b524e-70b5-4ea7-bc93-eee9f0fbeaed/download http://repositorio.bc.ufg.br/tede/bitstreams/6faedca3-c26d-4611-a6de-aa2c3500e495/download http://repositorio.bc.ufg.br/tede/bitstreams/e3cdcc86-3431-4c85-908a-e0f99a3bd117/download http://repositorio.bc.ufg.br/tede/bitstreams/86be415e-d797-471a-b738-d36e9a56a27b/download http://repositorio.bc.ufg.br/tede/bitstreams/cd8b5d51-6f2a-4b50-bc2c-d445880f98fd/download http://repositorio.bc.ufg.br/tede/bitstreams/9c5b9042-e4fa-4611-a482-eec2c67e4280/download |
| collection | Repositório Institucional da UFG |
| contributor_str_mv | Gomes, Ronaldo Barros Gomes, Ronaldo Barros Guimarães, Gilson Natal Pereira, Cláudio Henrique de Almeida Feitosa |
| dc.contributor.advisor1.fl_str_mv | Gomes, Ronaldo Barros |
| dc.contributor.advisor1Lattes.fl_str_mv | http://lattes.cnpq.br/6046088082653028 |
| dc.contributor.author.fl_str_mv | Rocha, Adilson Pereira da |
| dc.contributor.referee1.fl_str_mv | Gomes, Ronaldo Barros |
| dc.contributor.referee2.fl_str_mv | Guimarães, Gilson Natal |
| dc.contributor.referee3.fl_str_mv | Pereira, Cláudio Henrique de Almeida Feitosa |
| dc.date.accessioned.fl_str_mv | 2015-02-23T17:21:40Z |
| dc.date.issued.fl_str_mv | 2011-04-28 |
| dc.format.none.fl_str_mv | application/pdf |
| dc.identifier.citation.fl_str_mv | ROCHA, Adilson Pereira da. Estudo da aderência no reparo com concreto autoadensável (CAA): influência do preparo da superfície, da resistência à compressão do concreto da base e do tipo do concreto (convencional e CAA). 2011. 192 f. Dissertação (Mestrado em Engenharia Civil) - Universidade Federal de Goiás, Goiânia, 2011. |
| dc.identifier.uri.fl_str_mv | http://repositorio.bc.ufg.br/tede/handle/tede/4190 |
| dc.language.iso.fl_str_mv | por |
| dc.publisher.country.fl_str_mv | Brasil |
| dc.publisher.department.fl_str_mv | Escola de Engenharia Civil - EEC (RG) |
| dc.publisher.initials.fl_str_mv | UFG |
| dc.publisher.none.fl_str_mv | Universidade Federal de Goiás |
| dc.publisher.program.fl_str_mv | Programa de Pós-graduação em Engenharia Civil (EEC) |
| dc.relation.cnpq.fl_str_mv | 7962414133013518621 |
| dc.relation.confidence.fl_str_mv | 600 600 600 600 |
| dc.relation.department.fl_str_mv | 724087251626315585 |
| dc.relation.program.fl_str_mv | -6536446489817675175 |
| dc.relation.sponsorship.fl_str_mv | 2075167498588264571 |
| dc.rights.driver.fl_str_mv | http://creativecommons.org/licenses/by-nc-nd/4.0/ info:eu-repo/semantics/openAccess |
| dc.source.none.fl_str_mv | reponame:Repositório Institucional da UFG instname:Universidade Federal de Goiás (UFG) instacron:UFG |
| dc.subject.cnpq.fl_str_mv | ENGENHARIA CIVIL::ESTRUTURAS |
| dc.subject.eng.fl_str_mv | Bonding Concrete Preparation Surface conditions |
| dc.subject.por.fl_str_mv | Aderência Concreto Preparo Condição da superfície |
| dc.title.alternative.eng.fl_str_mv | Bond study on self-compacting concrete repairs: the influence of surface preparation, base concrete compressive strenght and the concrete type (conventional and SCC) |
| dc.title.eng.fl_str_mv | Estudo da aderência no reparo com concreto autoadensável (CAA): influência do preparo da superfície, da resistência à compressão do concreto da base e do tipo do concreto (convencional e CAA) |
| dc.type.driver.fl_str_mv | info:eu-repo/semantics/masterThesis |
| dc.type.status.fl_str_mv | info:eu-repo/semantics/publishedVersion |
| description | Efficient repairs in concrete structures require perfect bonding between the base concrete and the applied concrete. The experimental analysis shown in this study focused on how bonding is influenced by three types of base concrete preparation: hydro-jet blasting (BHD), manual scabbling (BMA) and mechanical scabbling (BME), as well as two types of base surface condition: dry (0%) and humid (100%) and also by the application of three different types of bonding agents: B - cement + water; C – cement + water + additive superplasticizer; D – cement + water + additive superplasticizer + active sílica. Fifteen conventional concrete bases prepared using concrete with compressive strength of class C20 and fifteen self-consolidating concrete bases with compressive strength of class C30 were tested. Surface roughness was characterized using profiles according to parameters Ra (standard deviation with respect to an average line) and Rz (average height between consecutives peaks and valleys). Self-consolidating concrete with C40 compressive strength was used to repair the concrete bases. Dyna Proceq apparatus was used to determine tension bonding strength. The hydro-jet blasting (BHD) preparation presented the lowest surface roughness values and the highest bonding strength results as well as the lowest values of the coefficient of variation. The manual scabbling (BMA) preparation presented intermediary results. The mechanical scabbling (BME) preparation presented the highest surface roughness values and the lowest bonding strength results. Surface humidity increase the number of concrete base ruptures. The use of bonding agents increased bonding strength regardless of the degree of surface humidity. |
| eu_rights_str_mv | openAccess |
| format | masterThesis |
| id | UFG-2_b0c83bab633d7dd0fbbfb29a4dc5d9cd |
| identifier_str_mv | ROCHA, Adilson Pereira da. Estudo da aderência no reparo com concreto autoadensável (CAA): influência do preparo da superfície, da resistência à compressão do concreto da base e do tipo do concreto (convencional e CAA). 2011. 192 f. Dissertação (Mestrado em Engenharia Civil) - Universidade Federal de Goiás, Goiânia, 2011. |
| instacron_str | UFG |
| institution | UFG |
| instname_str | Universidade Federal de Goiás (UFG) |
| language | por |
| network_acronym_str | UFG-2 |
| network_name_str | Repositório Institucional da UFG |
| oai_identifier_str | oai:repositorio.bc.ufg.br:tede/4190 |
| publishDate | 2011 |
| publishDateSort | 2011 |
| publisher.none.fl_str_mv | Universidade Federal de Goiás |
| reponame_str | Repositório Institucional da UFG |
| repository.mail.fl_str_mv | grt.bc@ufg.br |
| repository.name.fl_str_mv | Repositório Institucional da UFG - Universidade Federal de Goiás (UFG) |
| repository_id_str | oai:repositorio.bc.ufg.br:tede/1234 |
| rights_invalid_str_mv | http://creativecommons.org/licenses/by-nc-nd/4.0/ |
| spelling | Gomes, Ronaldo Barroshttp://lattes.cnpq.br/6046088082653028Gomes, Ronaldo BarrosGuimarães, Gilson NatalPereira, Cláudio Henrique de Almeida FeitosaRocha, Adilson Pereira da2015-02-23T17:21:40Z2011-04-28ROCHA, Adilson Pereira da. Estudo da aderência no reparo com concreto autoadensável (CAA): influência do preparo da superfície, da resistência à compressão do concreto da base e do tipo do concreto (convencional e CAA). 2011. 192 f. Dissertação (Mestrado em Engenharia Civil) - Universidade Federal de Goiás, Goiânia, 2011.http://repositorio.bc.ufg.br/tede/handle/tede/4190Efficient repairs in concrete structures require perfect bonding between the base concrete and the applied concrete. The experimental analysis shown in this study focused on how bonding is influenced by three types of base concrete preparation: hydro-jet blasting (BHD), manual scabbling (BMA) and mechanical scabbling (BME), as well as two types of base surface condition: dry (0%) and humid (100%) and also by the application of three different types of bonding agents: B - cement + water; C – cement + water + additive superplasticizer; D – cement + water + additive superplasticizer + active sílica. Fifteen conventional concrete bases prepared using concrete with compressive strength of class C20 and fifteen self-consolidating concrete bases with compressive strength of class C30 were tested. Surface roughness was characterized using profiles according to parameters Ra (standard deviation with respect to an average line) and Rz (average height between consecutives peaks and valleys). Self-consolidating concrete with C40 compressive strength was used to repair the concrete bases. Dyna Proceq apparatus was used to determine tension bonding strength. The hydro-jet blasting (BHD) preparation presented the lowest surface roughness values and the highest bonding strength results as well as the lowest values of the coefficient of variation. The manual scabbling (BMA) preparation presented intermediary results. The mechanical scabbling (BME) preparation presented the highest surface roughness values and the lowest bonding strength results. Surface humidity increase the number of concrete base ruptures. The use of bonding agents increased bonding strength regardless of the degree of surface humidity.A busca pela execução eficiente de um reparo em estruturas de concreto passa pela procura de uma aderência perfeita entre o concreto aplicado e o substrato. Durante a análise experimental, realizada nesta dissertação, analisou-se a influência de três tipos de preparo dos substratos – preparo com hidrojateadora (BHD), apicoamento manual (BMA) e apicoamento mecânico (BME), duas condições de superfície: seca (0%) e úmida (100%) e da aplicação de três tipos de ponte de aderência: B – cimento + água; C – cimento + água + aditivo superplastificante e D – cimento + água + aditivo superplastificante + sílica ativa, no sistema de aderência. Para a representação do substrato foram confeccionadas quinze bases de concreto convencional CCV de classe C20 e quinze de concreto autoadensável CAA de classe C30. A rugosidade foi caracterizada através dos perfis, de acordo com os parâmetros Ra (desvio padrão em relação à linha média) e Rz (altura média entre o pico e o vale consecutivo). Para concretagem do reparo utilizou-se o concreto autoadensável CAA de classe C40. O aparelho Dyna Proceq foi utilizado para as determinações de resistência de aderência à tração. O preparo com hidrojateadora (BHD) apresentou os menores valores de rugosidade e os maiores resultados de resistência de aderência, além de menores valores de coeficientes de variação. O preparo por apicoamento manual (BMA) apresentou resultados intermediários. O preparo por apicoamento mecânico (BME) apresentou os maiores valores de rugosidade e os menores resultados de resistência de aderência. O umedecimento da superfície promoveu um maior número de rupturas no substrato. O uso de pontes de aderência contribuiu para o aumento da resistência de aderência independentemente da condição de umidade da superfície.Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://repositorio.bc.ufg.br/tede/retrieve/16979/Disserta%c3%a7%c3%a3o%20-%20Adilson%20Pereira%20da%20Rocha%20-%202011.pdf.jpgporUniversidade Federal de GoiásPrograma de Pós-graduação em Engenharia Civil (EEC)UFGBrasilEscola de Engenharia Civil - EEC (RG)http://creativecommons.org/licenses/by-nc-nd/4.0/info:eu-repo/semantics/openAccessAderênciaConcretoPreparoCondição da superfícieBondingConcretePreparationSurface conditionsENGENHARIA CIVIL::ESTRUTURASEstudo da aderência no reparo com concreto autoadensável (CAA): influência do preparo da superfície, da resistência à compressão do concreto da base e do tipo do concreto (convencional e CAA)Bond study on self-compacting concrete repairs: the influence of surface preparation, base concrete compressive strenght and the concrete type (conventional and SCC)info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-653644648981767517560060060060072408725162631558579624141330135186212075167498588264571reponame:Repositório Institucional da UFGinstname:Universidade Federal de Goiás (UFG)instacron:UFGLICENSElicense.txtlicense.txttext/plain; charset=utf-82165http://repositorio.bc.ufg.br/tede/bitstreams/bf2e0baa-2629-47e4-a61a-51d9d98482ba/downloadbd3efa91386c1718a7f26a329fdcb468MD51CC-LICENSElicense_urllicense_urltext/plain; charset=utf-849http://repositorio.bc.ufg.br/tede/bitstreams/b25b524e-70b5-4ea7-bc93-eee9f0fbeaed/download4afdbb8c545fd630ea7db775da747b2fMD52license_textlicense_texttext/html; charset=utf-822376http://repositorio.bc.ufg.br/tede/bitstreams/6faedca3-c26d-4611-a6de-aa2c3500e495/downloadb292a83e42bd8ad62533bba1395b83ffMD53license_rdflicense_rdfapplication/rdf+xml; charset=utf-823148http://repositorio.bc.ufg.br/tede/bitstreams/e3cdcc86-3431-4c85-908a-e0f99a3bd117/download9da0b6dfac957114c6a7714714b86306MD54ORIGINALDissertação - Adilson Pereira da Rocha - 2011.pdfDissertação - Adilson Pereira da Rocha - 2011.pdfapplication/pdf6422992http://repositorio.bc.ufg.br/tede/bitstreams/86be415e-d797-471a-b738-d36e9a56a27b/download6084758e786d92b3d0b54e276271b54fMD55TEXTDissertação - Adilson Pereira da Rocha - 2011.pdf.txtDissertação - Adilson Pereira da Rocha - 2011.pdf.txtExtracted Texttext/plain325235http://repositorio.bc.ufg.br/tede/bitstreams/cd8b5d51-6f2a-4b50-bc2c-d445880f98fd/downloadff640dc4766163a366eb69d0dd2517b2MD56THUMBNAILDissertação - Adilson Pereira da Rocha - 2011.pdf.jpgDissertação - Adilson Pereira da Rocha - 2011.pdf.jpgGenerated Thumbnailimage/jpeg1987http://repositorio.bc.ufg.br/tede/bitstreams/9c5b9042-e4fa-4611-a482-eec2c67e4280/download5c1b699b8d954fb5aee53f4de7f829ffMD57tede/41902015-02-24 03:01:30.519http://creativecommons.org/licenses/by-nc-nd/4.0/Acesso Abertoopen.accessoai:repositorio.bc.ufg.br:tede/4190http://repositorio.bc.ufg.br/tedeRepositório InstitucionalPUBhttps://repositorio.bc.ufg.br/tedeserver/oai/requestgrt.bc@ufg.bropendoar:oai:repositorio.bc.ufg.br:tede/12342015-02-24T06:01:30Repositório Institucional da UFG - Universidade Federal de Goiás (UFG)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 |
| spellingShingle | Estudo da aderência no reparo com concreto autoadensável (CAA): influência do preparo da superfície, da resistência à compressão do concreto da base e do tipo do concreto (convencional e CAA) Rocha, Adilson Pereira da Aderência Concreto Preparo Condição da superfície Bonding Concrete Preparation Surface conditions ENGENHARIA CIVIL::ESTRUTURAS |
| status_str | publishedVersion |
| title | Estudo da aderência no reparo com concreto autoadensável (CAA): influência do preparo da superfície, da resistência à compressão do concreto da base e do tipo do concreto (convencional e CAA) |
| title_full | Estudo da aderência no reparo com concreto autoadensável (CAA): influência do preparo da superfície, da resistência à compressão do concreto da base e do tipo do concreto (convencional e CAA) |
| title_fullStr | Estudo da aderência no reparo com concreto autoadensável (CAA): influência do preparo da superfície, da resistência à compressão do concreto da base e do tipo do concreto (convencional e CAA) |
| title_full_unstemmed | Estudo da aderência no reparo com concreto autoadensável (CAA): influência do preparo da superfície, da resistência à compressão do concreto da base e do tipo do concreto (convencional e CAA) |
| title_short | Estudo da aderência no reparo com concreto autoadensável (CAA): influência do preparo da superfície, da resistência à compressão do concreto da base e do tipo do concreto (convencional e CAA) |
| title_sort | Estudo da aderência no reparo com concreto autoadensável (CAA): influência do preparo da superfície, da resistência à compressão do concreto da base e do tipo do concreto (convencional e CAA) |
| topic | Aderência Concreto Preparo Condição da superfície Bonding Concrete Preparation Surface conditions ENGENHARIA CIVIL::ESTRUTURAS |
| url | http://repositorio.bc.ufg.br/tede/handle/tede/4190 |