Estudo da molhabilidade de vidrado composto de resíduo de rochas ornamentais em cerâmica vermelha

Bibliographic Details
Main Author: Carvalho, Romário Alves
Publication Date: 2017
Format: Master thesis
Language: por
Source: Repositório Institucional da Universidade Federal do Espírito Santo (riUfes)
Download full: http://repositorio.ufes.br/handle/10/7827
Summary: The dimension stone industry generates large amounts of solid waste and an alternative to reduce this environmental liability is its use in the production of glazes. The objective of this work was to study the wettability of glaze made of dimension stone waste in red ceramic using the method of Sessile Drop. Six glaze compositions were prepared containing 49 to 77% of residue. The glaze was pressed with dimensions of 3mm x 3mm x 3mm and placed on a sintered red ceramic plate, and both were heated to fusion of the glaze up to temperature of 1100ºC. The variation of the contact angle was measured as a function of temperature, and the tests were repeated in specific isotherms to evaluate the kinetics of transformation. The contact angles from 1100°C change between 9 – 98° depending on the composition, indicating some glaze wet the surface of the ceramic satisfactorily while others do not spread, and therefore would not be indicated as composition for coating ceramic. The interface between the glaze and red ceramic showed physical interaction, indicating no reaction layer between the constituents.
id UFES_12a54fbd767f0b6461d35f56f7be64ac
oai_identifier_str oai:repositorio.ufes.br:10/7827
network_acronym_str UFES
network_name_str Repositório Institucional da Universidade Federal do Espírito Santo (riUfes)
repository_id_str 2108
spelling Estudo da molhabilidade de vidrado composto de resíduo de rochas ornamentais em cerâmica vermelhaWettability study of red ceramic and glaze coming from dimension stone wasteResidueGlazeWettabilitySessile DropCeramicContact AngleResíduoVidradoMolhabilidadeGota SéssilCerâmica de revestimentoÂngulo de ContatoCerâmicaRochas ornamentaisEngenharia Química66.0The dimension stone industry generates large amounts of solid waste and an alternative to reduce this environmental liability is its use in the production of glazes. The objective of this work was to study the wettability of glaze made of dimension stone waste in red ceramic using the method of Sessile Drop. Six glaze compositions were prepared containing 49 to 77% of residue. The glaze was pressed with dimensions of 3mm x 3mm x 3mm and placed on a sintered red ceramic plate, and both were heated to fusion of the glaze up to temperature of 1100ºC. The variation of the contact angle was measured as a function of temperature, and the tests were repeated in specific isotherms to evaluate the kinetics of transformation. The contact angles from 1100°C change between 9 – 98° depending on the composition, indicating some glaze wet the surface of the ceramic satisfactorily while others do not spread, and therefore would not be indicated as composition for coating ceramic. The interface between the glaze and red ceramic showed physical interaction, indicating no reaction layer between the constituents.O segmento de rochas ornamentais gera grande quantidade de resíduos sólidos e uma alternativa para reduzir esse passivo ambiental é a sua utilização na produção de vidrados. O objetivo deste trabalho foi estudar a molhabilidade do vidrado composto de resíduos de rochas ornamentais em cerâmica vermelha, empregando o método da Gota Séssil. Foram estudadas seis composições do vidrado contendo de 49 - 77% de resíduo. O vidrado foi prensado na dimensão de 3mm x 3mm x 3mm e colocado sobre uma placa de cerâmica vermelha sinterizada, e ambos foram aquecidos até a temperatura de 1100ºC. A fusão e a formação da gota líquida do vidrado sobre a cerâmica foram acompanhadas por imagens obtidas de uma câmera fotográfica acoplada ao forno. Pela análise dessas imagens foram obtidos os ângulos de contato em função da temperatura, e os ensaios foram repetidos em isotermas específicas para avaliar a cinética de transformação. Os ângulos de contatos a 1100ºC variaram de 9 - 98º dependendo da composição, indicando que alguns vidrados molham satisfatoriamente a superfície da cerâmica vermelha enquanto outros não espalham, e portanto, não seriam indicados como composição para cerâmica de revestimento. A interface entre o vidrado e a cerâmica vermelha apresentou interação física, não indicando camada reacional entre os constituintes.Universidade Federal do Espírito SantoBRMestrado em Engenharia QuímicaUFESPrograma de Pós-Graduação em Engenharia QuímicaBorges, Simone Pereira TaguchiBorges Júnior, Luiz AntônioGuimarães, DamaresNeves, Mirna AparecidaCarvalho, Romário Alves2018-08-01T22:57:14Z2018-08-012018-08-01T22:57:14Z2017-02-21info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisTextapplication/pdfhttp://repositorio.ufes.br/handle/10/7827porinfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da Universidade Federal do Espírito Santo (riUfes)instname:Universidade Federal do Espírito Santo (UFES)instacron:UFES2024-06-24T08:59:46Zoai:repositorio.ufes.br:10/7827Repositório InstitucionalPUBhttp://repositorio.ufes.br/oai/requestriufes@ufes.bropendoar:21082024-06-24T08:59:46Repositório Institucional da Universidade Federal do Espírito Santo (riUfes) - Universidade Federal do Espírito Santo (UFES)false
dc.title.none.fl_str_mv Estudo da molhabilidade de vidrado composto de resíduo de rochas ornamentais em cerâmica vermelha
Wettability study of red ceramic and glaze coming from dimension stone waste
title Estudo da molhabilidade de vidrado composto de resíduo de rochas ornamentais em cerâmica vermelha
spellingShingle Estudo da molhabilidade de vidrado composto de resíduo de rochas ornamentais em cerâmica vermelha
Carvalho, Romário Alves
Residue
Glaze
Wettability
Sessile Drop
Ceramic
Contact Angle
Resíduo
Vidrado
Molhabilidade
Gota Séssil
Cerâmica de revestimento
Ângulo de Contato
Cerâmica
Rochas ornamentais
Engenharia Química
66.0
title_short Estudo da molhabilidade de vidrado composto de resíduo de rochas ornamentais em cerâmica vermelha
title_full Estudo da molhabilidade de vidrado composto de resíduo de rochas ornamentais em cerâmica vermelha
title_fullStr Estudo da molhabilidade de vidrado composto de resíduo de rochas ornamentais em cerâmica vermelha
title_full_unstemmed Estudo da molhabilidade de vidrado composto de resíduo de rochas ornamentais em cerâmica vermelha
title_sort Estudo da molhabilidade de vidrado composto de resíduo de rochas ornamentais em cerâmica vermelha
author Carvalho, Romário Alves
author_facet Carvalho, Romário Alves
author_role author
dc.contributor.none.fl_str_mv Borges, Simone Pereira Taguchi
Borges Júnior, Luiz Antônio
Guimarães, Damares
Neves, Mirna Aparecida
dc.contributor.author.fl_str_mv Carvalho, Romário Alves
dc.subject.por.fl_str_mv Residue
Glaze
Wettability
Sessile Drop
Ceramic
Contact Angle
Resíduo
Vidrado
Molhabilidade
Gota Séssil
Cerâmica de revestimento
Ângulo de Contato
Cerâmica
Rochas ornamentais
Engenharia Química
66.0
topic Residue
Glaze
Wettability
Sessile Drop
Ceramic
Contact Angle
Resíduo
Vidrado
Molhabilidade
Gota Séssil
Cerâmica de revestimento
Ângulo de Contato
Cerâmica
Rochas ornamentais
Engenharia Química
66.0
description The dimension stone industry generates large amounts of solid waste and an alternative to reduce this environmental liability is its use in the production of glazes. The objective of this work was to study the wettability of glaze made of dimension stone waste in red ceramic using the method of Sessile Drop. Six glaze compositions were prepared containing 49 to 77% of residue. The glaze was pressed with dimensions of 3mm x 3mm x 3mm and placed on a sintered red ceramic plate, and both were heated to fusion of the glaze up to temperature of 1100ºC. The variation of the contact angle was measured as a function of temperature, and the tests were repeated in specific isotherms to evaluate the kinetics of transformation. The contact angles from 1100°C change between 9 – 98° depending on the composition, indicating some glaze wet the surface of the ceramic satisfactorily while others do not spread, and therefore would not be indicated as composition for coating ceramic. The interface between the glaze and red ceramic showed physical interaction, indicating no reaction layer between the constituents.
publishDate 2017
dc.date.none.fl_str_mv 2017-02-21
2018-08-01T22:57:14Z
2018-08-01
2018-08-01T22:57:14Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://repositorio.ufes.br/handle/10/7827
url http://repositorio.ufes.br/handle/10/7827
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv Text
application/pdf
dc.publisher.none.fl_str_mv Universidade Federal do Espírito Santo
BR
Mestrado em Engenharia Química
UFES
Programa de Pós-Graduação em Engenharia Química
publisher.none.fl_str_mv Universidade Federal do Espírito Santo
BR
Mestrado em Engenharia Química
UFES
Programa de Pós-Graduação em Engenharia Química
dc.source.none.fl_str_mv reponame:Repositório Institucional da Universidade Federal do Espírito Santo (riUfes)
instname:Universidade Federal do Espírito Santo (UFES)
instacron:UFES
instname_str Universidade Federal do Espírito Santo (UFES)
instacron_str UFES
institution UFES
reponame_str Repositório Institucional da Universidade Federal do Espírito Santo (riUfes)
collection Repositório Institucional da Universidade Federal do Espírito Santo (riUfes)
repository.name.fl_str_mv Repositório Institucional da Universidade Federal do Espírito Santo (riUfes) - Universidade Federal do Espírito Santo (UFES)
repository.mail.fl_str_mv riufes@ufes.br
_version_ 1834478831740649472

Similar Items