Analysis of fatigue crack propagation on load patterns produced by trains on railway bridges

Bibliographic Details
Main Author: Narciso, Tiago André Rodrigues
Publication Date: 2024
Format: Master thesis
Language: eng
Source: Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
Download full: https://hdl.handle.net/10316/116545
Summary: Dissertação de Mestrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
id RCAP_6aa2593f7af10c6413e6f91016b8b092
oai_identifier_str oai:estudogeral.uc.pt:10316/116545
network_acronym_str RCAP
network_name_str Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
repository_id_str https://opendoar.ac.uk/repository/7160
spelling Analysis of fatigue crack propagation on load patterns produced by trains on railway bridgesAnálise da propagação de fendas por fadiga em padrões de carga produzidos por comboios em pontes ferroviáriasFatigue Crack GrowthVariable Amplitude LoadingComplex LoadingsNumerical SimulationCrack ClosureCrescimento de Fendas por FadigaCarregamento de Amplitude VariávelCarregamentos ComplexosSimulação NuméricaFecho de FendaDissertação de Mestrado em Engenharia Mecânica apresentada à Faculdade de Ciências e TecnologiaA maioria dos componentes mecânicos está sujeita a cargas cíclicas ou dinâmicas que podem provocar fenómenos de falhas destes componentes. A fadiga é o fenómeno de falha mais comum em componentes sujeitos a estas condições. Deste modo é importante dimensionar os componentes à fadiga e prever a sua vida útil para evitar falhas com consequências muito graves. A previsão da vida útil é normalmente feita a partir da evolução da propagação das fendas por fadiga, onde se utiliza as curvas /−Δ. No entanto, esta abordagem apresenta sempre algumas limitações porque os fenómenos que acontecem na extremidade da fenda são irreversíveis, atuando no regime plástico, e o fator de intensidade de tensão, Δ, é um parâmetro meramente elástico. Para contornar esta limitação, outros parâmetros não lineares foram propostos, um deles é o CTOD plástico que vai ser abordado neste trabalho para explicar alguns fenómenos que acontecem na propagação de fendas por fadiga.Esta dissertação tem como objetivo principal estudar o efeito dos carregamentos de amplitude variável na propagação de fendas por fadiga em provetes de tensão compacta (CT) de uma liga AA2024-T351. Para isso, foram estudados dois carregamentos reais de comboios a passar sobre pontes ferroviárias. Os carregamentos foram filtrados através do método de Rainflow. Recorreu-se à análise de métodos de elementos finitos (MEF) para a resolução do problema, o programa de elementos finitos DD3IMP efetuou a simulação numérica de resultados. Para os dois carregamentos foi ainda feita uma comparação com carregamentos constantes para analisar possíveis semelhanças que podiam simplificar o estudo de carregamentos complexos. A importância do fecho de fenda também foi considerada neste estudo ao analisar numericamente os dois carregamentos complexos numa situação hipotética que se desprezou o contacto entre os flancos dos provetes CT. Também se testou a influência dos ciclos elásticos no padrão, comparando o carregamento principal com outro em que se considerou a omissão destes ciclos. Com este estudo, conclui-se que o fecho de fenda é um fator bastante importância para os carregamentos complexos com valores de amplitude elevados. Também se verificou que a omissão dos ciclos elásticos praticamente não tem influência na propagação da fenda por fadiga, simplificando a análise de carregamentos complexos.Most mechanical components are subjected to cyclic or dynamic loads that can cause them to fail. Fatigue is the most common failure phenomenon in components exposed to these conditions. Therefore, to avoid failures with very serious consequences, it is important to design components for fatigue and predict their service life. Life prediction is usually studied based on the evolution of Fatigue Crack Growth (FCG) using the /-Δ curves. However, this approach has some limitations because the phenomena that occur at the crack tip are irreversible and operate in the plastic domain, while the stress intensity factor, Δ, is a purely elastic parameter. To overcome this limitation, other non-linear parameters have been proposed, one of which is the plastic Crack Tip Opening Displacement (CTOD), which will be discussed in this study to explain some phenomena that occur in fatigue crack propagation.The main objective of this thesis is to analyse the effect of variable amplitude loading on fatigue crack propagation, in Compact Tension (CT) specimens made from an AA2024-T351 alloy. This work focused on complex loading, so two real loads of trains passing over railway bridges were studied. The loads were filtered using the Rainflow method. The Finite Element Method (FEM) was used to solve the problem and the Finite Element program DD3IMP was used to simulate the results numerically. The two loads were also compared with constant loads to analyse possible similarities that could simplify the study of complex loads. The importance of crack closure was considered in this study by numerically analysing the two complex loads in a hypothetical situation where the contact between the flanks of the CT specimens was not considered. The influence of elastic cycles on the pattern was tested by comparing the main load with another one, in which these cycles were omitted.It was concluded from this study that crack closure is a very important factor for complex loads with high amplitude values. It was also found that the omission of elastic cycles has practically no effect on fatigue crack propagation, which is a simplification in the analysis of complex loads.2024-07-25info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttps://hdl.handle.net/10316/116545https://hdl.handle.net/10316/116545TID:203694678engNarciso, Tiago André Rodriguesinfo:eu-repo/semantics/openAccessreponame:Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)instname:FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologiainstacron:RCAAP2024-09-11T22:08:08Zoai:estudogeral.uc.pt:10316/116545Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireinfo@rcaap.ptopendoar:https://opendoar.ac.uk/repository/71602025-05-29T06:10:15.805528Repositórios Científicos de Acesso Aberto de Portugal (RCAAP) - FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologiafalse
dc.title.none.fl_str_mv Analysis of fatigue crack propagation on load patterns produced by trains on railway bridges
Análise da propagação de fendas por fadiga em padrões de carga produzidos por comboios em pontes ferroviárias
title Analysis of fatigue crack propagation on load patterns produced by trains on railway bridges
spellingShingle Analysis of fatigue crack propagation on load patterns produced by trains on railway bridges
Narciso, Tiago André Rodrigues
Fatigue Crack Growth
Variable Amplitude Loading
Complex Loadings
Numerical Simulation
Crack Closure
Crescimento de Fendas por Fadiga
Carregamento de Amplitude Variável
Carregamentos Complexos
Simulação Numérica
Fecho de Fenda
title_short Analysis of fatigue crack propagation on load patterns produced by trains on railway bridges
title_full Analysis of fatigue crack propagation on load patterns produced by trains on railway bridges
title_fullStr Analysis of fatigue crack propagation on load patterns produced by trains on railway bridges
title_full_unstemmed Analysis of fatigue crack propagation on load patterns produced by trains on railway bridges
title_sort Analysis of fatigue crack propagation on load patterns produced by trains on railway bridges
author Narciso, Tiago André Rodrigues
author_facet Narciso, Tiago André Rodrigues
author_role author
dc.contributor.author.fl_str_mv Narciso, Tiago André Rodrigues
dc.subject.por.fl_str_mv Fatigue Crack Growth
Variable Amplitude Loading
Complex Loadings
Numerical Simulation
Crack Closure
Crescimento de Fendas por Fadiga
Carregamento de Amplitude Variável
Carregamentos Complexos
Simulação Numérica
Fecho de Fenda
topic Fatigue Crack Growth
Variable Amplitude Loading
Complex Loadings
Numerical Simulation
Crack Closure
Crescimento de Fendas por Fadiga
Carregamento de Amplitude Variável
Carregamentos Complexos
Simulação Numérica
Fecho de Fenda
description Dissertação de Mestrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
publishDate 2024
dc.date.none.fl_str_mv 2024-07-25
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/10316/116545
https://hdl.handle.net/10316/116545
TID:203694678
url https://hdl.handle.net/10316/116545
identifier_str_mv TID:203694678
dc.language.iso.fl_str_mv eng
language eng
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.source.none.fl_str_mv reponame:Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
instname:FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologia
instacron:RCAAP
instname_str FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologia
instacron_str RCAAP
institution RCAAP
reponame_str Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
collection Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
repository.name.fl_str_mv Repositórios Científicos de Acesso Aberto de Portugal (RCAAP) - FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologia
repository.mail.fl_str_mv info@rcaap.pt
_version_ 1833602600515141632

Similar Items