Processamento e caracterização mecânica e metalográfica de compósitos adiamantados à base de cobre-níquel obtidos por hot pressing

Bibliographic Details
Main Author: Ferreira, Pedro Alexandre Monteiro
Publication Date: 2015
Format: Master thesis
Language: por
Source: Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
Download full: http://hdl.handle.net/1822/39343
Summary: Dissertação de mestrado em Engenharia de Materiais
id RCAP_598c845bdea48e79dab8df3ef6715a02
oai_identifier_str oai:repositorium.sdum.uminho.pt:1822/39343
network_acronym_str RCAP
network_name_str Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
repository_id_str https://opendoar.ac.uk/repository/7160
spelling Processamento e caracterização mecânica e metalográfica de compósitos adiamantados à base de cobre-níquel obtidos por hot pressingMechanical and metallurgical characterization of hot pressed diamond reinforced copper-nickel alloysCompósitos adiamantadosFerramentas de corteFerramentas de corte adiamantadasPrensagem a quenteCutting toolsDiamond compositesDiamond cutting toolsHot pressingEngenharia e Tecnologia::Engenharia MecânicaDissertação de mestrado em Engenharia de MateriaisNo mercado da prospeção de rochas existe uma grande procura por ferramentas que possuam características e propriedades adequadas às rochas onde são aplicadas, nomeadamente com resistência mecânica e comportamento ao desgaste adequados. Neste contexto é fundamental um estudo contínuo para encontrar os melhores materiais que possam ser utilizados na produção deste tipo de ferramentas. Atualmente as ferramentas de corte adiamantadas utilizam como principal matriz metálica o cobalto, mas dado que a sua utilização apresenta algumas desvantagens, como é o caso da sua toxicidade e do seu elevado preço, tem vindo a estudar-se a possibilidade de se implementar outro tipo de matriz metálica. O presente trabalho tem como finalidade o estudo de compósitos adiamantados à base de uma matriz de cobre-níquel, de modo a aferir do seu potencial para utilização em ferramentas de corte adiamantadas. O trabalho apresentado faz inicialmente um enquadramento teórico acerca das ferramentas de corte adiamantadas, dando a conhecer toda a sua envolvência e materiais que são usualmente utilizados neste tipo de ferramentas, bem como os prós e contras da sua utilização. Posteriormente, o trabalho foca-se no estudo da aplicabilidade de uma matriz de cobre-níquel neste tipo de ferramentas, realizando a caracterização mecânica e metalográfica de compósitos adiamantados que apresentam por base esta matriz. Foi também estudado se a adição de certos elementos/compostos (Sn e WC) poderiam melhorar as propriedades mecânicas e o comportamento ao desgaste da matriz de Cu-Ni. Deste modo foram produzidas amostras com adição de Sn e/ou WC. Ao longo do trabalho apresentado são dadas a conhecer (estudadas) as condições de processamento utilizadas para a produção destes compósitos, os ensaios realizados para a sua caracterização (ensaios de dureza, testes de corte e ensaios de desgaste) e os resultados obtidos. Uma inovação deste trabalho foi a utilização, nos ensaios de desgaste, de pedras graníticas, introduzindo uma maior proximidade entre o ensaio laboratorial e a realidade sobre a qual se foca este estudo. Com a realização desta tese foi possível concluir que a adição de Sn à matriz Cu-Ni mostrou ser bastante positiva, melhorando as suas propriedades mecânicas e comportamento ao desgaste. Foi assim possível encontrar um compósito que poderá substituir o Co na produção das ferramentas de corte adiamantas, sendo este o Cu-Ni-Sn-10WC reforçado com diamante. No entanto caso as condições em que os pinos fossem idênticas entre si (mesma dispersão e mesmo número de partículas expostas), o resultado espectável seria que o compósito Cu-Ni-10Sn reforçado com diamante fosse a melhor solução, pois foi nesta matriz que se observaram as melhores propriedades e comportamento ao desgaste.On the market of prospecting of rocks there is a great demand for tools that possess characteristics and properties appropriate to the rocks where they are applied, particularly with appropriate mechanical resistance and wear performance. In this context it is essential to study continuously in order to find the best materials that can be used in the production of this type of tools. Currently, diamond cutting tools use cobalt as main metal matrix, but this material drawbacks, such as its toxicity and high cost, has dictated the need to study new possibilities for metallic matrices. The present work intends to study composite tools based on a copper-nickel metal matrix, in order to assess its potential for use in diamond cutting tools. The thesis here presented starts with a theoretical framework about diamond cutting tools, focusing on all its related issues and materials that are usually used in this kind of tools, as well as the pros and cons of its use. Subsequently, the applicability of this copper-nickel matrix in this kind of tools is assessed, by performing the mechanical and metallographic characterization of the diamondreinforced composites that use this matrix. It was also studied whether the addition of certain elements/compounds (Sn and WC) could improve the mechanical properties and wear behaviour of Cu-Ni matrix, thus samples were produced with addition of Sn and WC. Throughout the work, the processing conditions used for the production of these composites are studied and presented, as well as the tests performed for their characterisation (hardness tests, shear tests and wear tests), finishing with the results obtained. An innovative aspect of this work was the use of granitic stones in the wear tests, introducing a greater proximity between laboratory tests and the reality on which is focused this study. This thesis allowed to conclude that the addition of Sn to the Cu-Ni matrix proved to be very positive, by improving its mechanical properties and wear behaviour. It was thus possible to find a composite that can effectively replace Co in the production of diamond cutting tools: the Cu-Ni-Sn-10WC reinforced with diamond. However if the conditions of the pins were identical to each other (same dispersion and same number of particles exposed), the expected result would be that the composite made of Cu-Ni-10Sn diamond reinforced would be the best solution, once it was the material with best mechanical and wear behaviour.Fundação para a Ciência e Tecnologia (FCT) - EXCL-EMS-TEC-0460/2012 e UID/EEE/04436/2013Silva, Filipe SamuelHenriques, Bruno Alexandre Pacheco de CastroUniversidade do MinhoFerreira, Pedro Alexandre Monteiro20152015-01-01T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfhttp://hdl.handle.net/1822/39343porinfo:eu-repo/semantics/openAccessreponame:Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)instname:FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologiainstacron:RCAAP2024-05-11T06:31:37Zoai:repositorium.sdum.uminho.pt:1822/39343Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireinfo@rcaap.ptopendoar:https://opendoar.ac.uk/repository/71602025-05-28T15:55:46.148730Repositórios Científicos de Acesso Aberto de Portugal (RCAAP) - FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologiafalse
dc.title.none.fl_str_mv Processamento e caracterização mecânica e metalográfica de compósitos adiamantados à base de cobre-níquel obtidos por hot pressing
Mechanical and metallurgical characterization of hot pressed diamond reinforced copper-nickel alloys
title Processamento e caracterização mecânica e metalográfica de compósitos adiamantados à base de cobre-níquel obtidos por hot pressing
spellingShingle Processamento e caracterização mecânica e metalográfica de compósitos adiamantados à base de cobre-níquel obtidos por hot pressing
Ferreira, Pedro Alexandre Monteiro
Compósitos adiamantados
Ferramentas de corte
Ferramentas de corte adiamantadas
Prensagem a quente
Cutting tools
Diamond composites
Diamond cutting tools
Hot pressing
Engenharia e Tecnologia::Engenharia Mecânica
title_short Processamento e caracterização mecânica e metalográfica de compósitos adiamantados à base de cobre-níquel obtidos por hot pressing
title_full Processamento e caracterização mecânica e metalográfica de compósitos adiamantados à base de cobre-níquel obtidos por hot pressing
title_fullStr Processamento e caracterização mecânica e metalográfica de compósitos adiamantados à base de cobre-níquel obtidos por hot pressing
title_full_unstemmed Processamento e caracterização mecânica e metalográfica de compósitos adiamantados à base de cobre-níquel obtidos por hot pressing
title_sort Processamento e caracterização mecânica e metalográfica de compósitos adiamantados à base de cobre-níquel obtidos por hot pressing
author Ferreira, Pedro Alexandre Monteiro
author_facet Ferreira, Pedro Alexandre Monteiro
author_role author
dc.contributor.none.fl_str_mv Silva, Filipe Samuel
Henriques, Bruno Alexandre Pacheco de Castro
Universidade do Minho
dc.contributor.author.fl_str_mv Ferreira, Pedro Alexandre Monteiro
dc.subject.por.fl_str_mv Compósitos adiamantados
Ferramentas de corte
Ferramentas de corte adiamantadas
Prensagem a quente
Cutting tools
Diamond composites
Diamond cutting tools
Hot pressing
Engenharia e Tecnologia::Engenharia Mecânica
topic Compósitos adiamantados
Ferramentas de corte
Ferramentas de corte adiamantadas
Prensagem a quente
Cutting tools
Diamond composites
Diamond cutting tools
Hot pressing
Engenharia e Tecnologia::Engenharia Mecânica
description Dissertação de mestrado em Engenharia de Materiais
publishDate 2015
dc.date.none.fl_str_mv 2015
2015-01-01T00:00:00Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://hdl.handle.net/1822/39343
url http://hdl.handle.net/1822/39343
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
instname:FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologia
instacron:RCAAP
instname_str FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologia
instacron_str RCAAP
institution RCAAP
reponame_str Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
collection Repositórios Científicos de Acesso Aberto de Portugal (RCAAP)
repository.name.fl_str_mv Repositórios Científicos de Acesso Aberto de Portugal (RCAAP) - FCCN, serviços digitais da FCT – Fundação para a Ciência e a Tecnologia
repository.mail.fl_str_mv info@rcaap.pt
_version_ 1833595631706308608

Similar Items